Preparation and Characterization of Nano Functionalized Graphene/room Temperature Vulcanized Silicone Rubber Composites

马文石,邓帮君

DOI: https://doi.org/10.13801/j.cnki.fhclxb.2011.04.013

2011-01-01

Abstract:Graphite oxide was modified by KH-550,the modified graphite oxide was reduced to form functionalized graphene（FG） dispersing consistently in the acetone/water（mass ratio is 9∶1） solution by ultrasonic treatment before drying.The FG dispersion was intensively mixed for a certain time by ultrasonic treatment to disperse the nano-FG in α,ω-dihydroxy polydimethylsiloxane matrix and obtained an uniform and stable nano-FG/room temperature vulcanized（RTV） silicone rubber composite after curing.FTIR,TEM,SEM,XRD,and DSC analysis show that KH-550 bonds to the surface of FG sheet to make its layers wrinkled,folding and partially exfoliated,and broaden its layer spacing to 3.46.FG exfoliates into transparent or semi-transparent layers after ultrasonic treatment.The uniform and wrinkled cross-section morphology of nano-FG/RTV silicone rubber composite,which is different from that of pure silicone rubber,shows that there is no micro-phase separation between the two parts.Compared with the pure silicone rubber,the Tg,Tm and crystallinity of all the nano-FG/RTV silicone rubber composites are improved.Mechanical property tests show that nano-FG reinforces silicone rubber a lot.The tensile strength and the elongation at break of composite with 0.5wt% nano-FG are 0.43MPa and 265%,respectively.The tensile strength more than doubles and the elongation at break increases 52% compared with that of pure silicone rubber.