An Ultra Closely [pgr]-Stacked Organic Semiconductor for High Performance Field-Effect Transistors
Liqiang Li,Qingxin Tang,Hongxiang Li,Xiaodi Yang,Wenping Hu,Yabin Song,Zhigang Shuai,Wei Xu,Yunqi Liu,Daoben Zhu
2007-01-01
Abstract:Since the first organic field-effect transistor (OFET) was reported in 1986, there has been remarkable progress in the development of OFETs. However, there remain some key challenges in this field,namely the mobility (most OFETs with a mobility lower than 1 cm V s), on/off ratio and environmental stability. Moreover, quantum mechanical calculations and structural analysis have predicted that high mobility can be obtained when conjugated molecules have strong interactions with neighboring molecules to maximize the overlap of p molecular orbits. Hence, theoretically speaking, a p stacked structure is expected to provide more efficient orbital overlap and thereby facilitates carrier transport. However, so far, the organic semiconductors which exhibit high mobility and high on/off ratio usually possess herringbone structure, e.g., rubrene and pentacene, which results in reduced intermolecular electronic couplings. The fundamental aspects of carrier transport in OFETs, especially the role of solid-state packing, are still under scrutiny. It is imperative to establish the structure-properties relationship both experimentally and theoretically for the carrier mobility of organic semiconductors. Phthalocyanines have attracted attentions in OFETs for some years because of their remarkably chemical and thermal stabilities, as well as non-toxicity and good field-effect properties. TiOPc is known as one of the most efficient organic photoconductors in the near-IR region and is currently used in more than 90 % laser printers. In contrast to other phthalocyanines, e.g., copper phthalocyanine, TiOPc is a nonplanar and polar molecule with the titanyl group located perpendicular to the macro cycle, with the outer phenyl rings making an angle of 7° with respect to the C-N inner ring, so that the molecule has a shallow square-pyramid structure (Fig. 1a). Three crystal structures of TiOPc have been reported so far, a monoclinic phase I (hereafter b-TiOPc), a triclinic phase II (hereafter a-TiOPc), and a triclinic phase Y. In the triclinic a-structure, TiOPc molecules form concave and