Electrocatalysis for Oxygen Reduction by Ketjen Black EC 300J Supported Cobalt Porphyrin Complexes after High-temperature Pyrolysis

Zhang Hong,Ren Qi-Zhi,He Sheng-Yi,Wang Qing-Yu,Jiang Zong-Run

2010-01-01

Abstract:Carbon black EC 300J(KB) with high mesoporous area and electrical conductivity was used as support for cobalt tetramethoxyphenylporphyrin(CoTMPP) to prepare the cathode electrocatalysts(CoTMIPP/KB) for the oxygen reduction in proton exchange membrane fuel cell (PEMFC). The influence of chemical pretreatment of carbon black supports and 900 degrees C heat-treating of the electrocatalysts on the electrocatalytic activities for oxygen reduction of CoTIMPP/KB were investigated by cyclic voltammogram(CV). The results show that pretreatment with 6 mol/L HNO3 of carbon support and 900 degrees C heat-treatment of the catalyst, although the pyrolysis occurred for the CoTMPP structure, the electrocatalyst has the best catalytic performance for oxygen reduction, both the cathodic peak potential (E-p) and the maximum capacitive current(I-p) were improved. The surface properties and the microstructures of both the carbon black KB and the electrocatalyst were investigated by IR, MID, TEM and nitrogen adsorption/desorption. After the pretreatment with 6 mol/L HNO3 the concentration of hydroxyl group and other oxygen-groups were increased on KB surface and no obvious particle aggregation of KB was observed, an average particle size of about 30 nm of KB was observed; The pore structure of the catalysts is mainly composed of mesopores and has a narrow pore size distribution, which prove CoTMPP/KB to be a good electrocatalyst; CoC3 (101) and metallic Co(111) were formed in the catalyst after 900 degrees C heat-treatment, and the cobalt ions were well dispersed in the carbon black surface, with mean pore size of 8. 2 nm and surface area of 463. 4 m(2)/g.