Improved hydrogen storage properties of NaBH4 destabilized by CaH2 and Ca(BH4)2

Jianfeng Mao,Zaiping Guo,Xuebin Yu,Hua Liu

DOI: https://doi.org/10.1021/jp2020319

2011-01-01

Abstract:NaBH4, with a 10.6 wt % theoretical H-2 capacity, is a promising hydrogen storage candidate material. However, the high thermodynamic stability and slow H-exchange kinetics have to be improved for its practical use. In this study, NaBH4 was destabilized by using CaH2 or Ca(BH4)(2). Temperature-programmed desorption experiments revealed a significant improvement in the decomposition temperature and the rate of desorption, as well as the weight percentage of hydrogen released from composites with the additive upon heating to 500 degrees C. X-ray diffraction has confirmed the formation of CaB6 upon dehydrogenation, which stabilizes the dehydrogenated state of boron and, therefore, destabilizes the NaBH4. Interestingly, as a source of CaH2, the addition of Ca(BH4)(2) results in superior hydrogen desorption performance compared with that of CaH2. To fully characterize this composite system, xNaBH(4) + Ca(BH4)(2) composites, for several x values between 1 and 20, were systematically investigated by a series of dehydrogenation and structural analyses. Furthermore, partial reversibility of the NaBH4/Ca(BH4)(2) composite with and without NbF5 catalyst was also confirmed under moderate conditions. The mechanism underlying the characteristic enhancement in the NaBH4/CaH2 and NaBH4/Ca(BH4)(2) is also discussed.