Growth and Spectra Properties of Tm^3＋：BaY2F8 Crystal

TONELLIM

DOI: https://doi.org/10.14062/j.issn.0454-5648.2011.08.003

2011-01-01

Abstract:Tm^3＋：BaY2F8（Tm：BYF） single crystal was grown by the Czochralski method.The phase composition and spectra proper-ties of Tm3＋：BaY2F8 crystal was investigated via X-ray diffractometer and spectroscopy.The results show that the as-grown Tm：BYF crystal belongs to a monoclinic system with the space group C2/m.The cell parameters calculated were a = 0.699 28 nm,b = 1.052 93 nm,c = 0.427 51 nm,and β = 99.69°.The full width at half a maximum（FWHM） of the absorption peak located at 791 nm was 42 nm at room temperature in absorption spectra,and the absorption coefficient and absorption cross-section calculated were 4.56 cm^–1 and 8.09 × 10^–21 cm^2,respectively.The crystal excitated by 795 nm laser has an intensive fluorescence emission peak located at 1 879.6 nm,the FWHM and emission cross-section at 1 879.6 nm of 79 nm and 2.13 × 10^–21 cm^2,respectively,and the fluorescence lifetime of 8.7 ms at 1 879.6 nm,could favor to realize the 1.88 μm laser output.