Abstract:The Y2O2S:Er3+@Y2O2S:Yb3+,Tm3+ core-shell upconversion (UC) nanoparticles with average diameter of 95 nm were synthesized by the homogeneous co-precipitation method combining with the solid-gas sulfidation route. The increases of nanocrystaline size after the shell coating was observed both in the X-ray diffraction (XRD) and transmission electron microscope (TEM) measurements. This indicates the composition homogeneity core-shell Y2O2S nanocrystals. Meanwhile, the luminescence of both the Er3+ and Tm3+ ions are realized for the first time in the novel core-shell Y2O2S:Er3+@Y2O2S:Yb3+,Tm3+ nanoparticles under the excitations of both 980 and 1550 nm. When excited by a 980 nm laser diode, the Y2O2S:Er3+@Y2O2S:Yb3+,Tm3+ phosphor exhibits blue (approximate to 475 nm), green (approximate to 548 nm) and red (approximate to 670 nm) emissions in the visible region, which correspond to the (1)G(4) -> H-3(6) transition of Tm(3+)ions, S-4(3/2), H-2(11/2) -> I-4(15/2) and F-4(9/2) -> I-4(15/2) transitions of Er3+ ions, respectively. The very strong emission at the near infrared (NIR) region is mainly due to the H-3(4) -> H-3(6) transition of Tm3+ ions. The emission from both of Era} and Tm3+ ions under 980 nm excitation reveals the energy transfers of Yb3+ -> Tm3+ within the shell layer and Yb3+ -> Er3+ between the shell and the core. When pumping at 1550 nm, although only Er3+ ions can efficiently absorb the excitation energy, the strong UC emissions from Tm3+ ions were also observed. This is owing to the energy transfer between the core and the shell through Er3+ -> Yb3+ -> Tm3+ ions. (C) 2016 Elsevier B.V. All rights reserved.

Luminescence and Near-Infrared Emission of Rare Earth Core-Shell Nanomaterials Synthesized Via Mesoporous Silica Nanoparticles As Template

Preparation and optical properties of core-shell CAFZIYB, ER@SIOZ nanoparticles

Preparation and Optical Properties of Core-Shell CaF

Upconversion Luminescence Properties of Y 2 O 2 S:Er 3+ @Y 2 O 2 S:Yb 3+ ,tm 3+ Core-Shell Nanoparticles Prepared Via Homogeneous Co-Precipitation

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Synthesis and Luminescent Properties of Monodisperse Core–shell Structured SiO2@Lu2O3:Eu3+ Microspheres

Sequential Growth of Uniform β-NaYF4@β-NaLnF4 (Ln = Y, Lu, Yb) Microcrystals with Luminescent Properties of Multicolor Tuning and Dual-Mode Emission

Luminescent Character of Mesoporous Silica with Er2o3 Composite Materials

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Synthesis and Luminescence Properties of Water Soluble α-NaGdF4/β-NaYF4:Yb,Er Core-Shell Nanoparticles

Preparation and upconversion luminescence of beta-NaYF4:Yb3+, Tm3+/ZnO nanoparticles

Towards core-shell engineering for efficient luminescence and temperature sensing

Upconversion Luminescence Properties of Y2o3:Yb, Er and Y2o2s:Yb, Er Nanoparticles Prepared by Complex Precipitation

Template-Directed Synthesis And Upconversion Luminescence Of Y2o3 Hollow Spheres

Facile Synthesis and Luminescence of Uniform Y2O3 Hollow Spheres by a Sacrificial Template Route

Highly Efficient Near-Infrared II Electrochemiluminescence from NaYbF 4 Core Mesoporous Silica Shell Nanoparticles

Mesoporous Silica Encapsulating Upconversion Luminescence Rare-Earth Fluoride Nanorods for Secondary Excitation.

Synthesis and Photoluminescent Properties of NaYF<SUB>4</SUB>:Eu<SUP>3+</SUP> Core and NaYF<SUB>4</SUB>:Eu<SUP>3+</SUP>/NaYF<SUB>4</SUB> Core/Shell Nanocrystals

Energy Transfer and Enhanced Luminescence in Metal Oxide Nanoparticle and Rare Earth Codoped Silica

Uniform Mesoporous CaSiO 3 :Eu 3+ Nanospheres: Template-directed Synthesis, Luminescence and Sustained Drug Release Properties

Research Progress on the Study of Rare Earth Doped Y2O3 Nanocrystalline Luminescent Materials