Abstract:Monodisperse Ni/Pd core/shell nanoparticles (NPs) have been synthesized by sequential reduction of nickel(II) acetate and palladium(II) bromide in oleylamine (OAm) and trioctylphosphine (TOP). The Ni/Pd NPs have a narrow size distribution with a mean particle size of 10 nm and a standard deviation of 5% with respect to the particle diameter. Mechanistic studies showed that the presence of TOP was essential to control the reductive decomposition of Ni-TOP and Pd-TOP, and the formation of Ni/Pd core/shell NPs. Using the current synthetic protocol, the composition of the Ni/Pd within the core/shell structure can be readily tuned by simply controlling the initial molar ratio of the Ni and Pd salts. The as-synthesized Ni/Pd core/shell NPs were supported on graphene (G) and used as catalyst in Suzuki-Miyaura cross-coupling reactions. Among three different kinds of Ni/Pd NPs tested, the Ni/Pd (Ni/Pd = 3/2) NPs were found to be the most active catalyst for the Suzuki-Miyaura cross-coupling of arylboronic acids with aryl iodides, bromides and even chlorides in a dimethylformamide/water mixture by using K2CO3 as a base at 110 °C. The G-Ni/Pd was also stable and reusable, providing 98% conversion after the 5th catalytic run without showing any noticeable Ni/Pd composition change. The G-Ni/Pd structure reported in this paper combines both the efficiency of a homogeneous catalyst and the durability of a heterogeneous catalyst, and is promising catalyst candidate for various Pd-based catalytic applications.

Monodispersed Pd-Ni Nanoparticles: Composition Control Synthesis And Catalytic Properties In The Miyaura-Suzuki Reaction

Pd-Ni Nanoparticles Supported on Titanium Oxide As Effective Catalysts for Suzuki-Miyaura Coupling Reactions

Bimetallic Pd-Ni core-shell nanoparticles as effective catalysts for the Suzuki reaction

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Epitaxial Growth of Multimetallic Pd@PtM (M = Ni, Rh, Ru) Core-Shell Nanoplates Realized by in Situ-Produced CO from Interfacial Catalytic Reactions.

High-performance Heterogeneous Catalysis with Surface-Exposed Stable Metal Nanoparticles.

General Preparation for Pt-Based Alloy Nanoporous Nanoparticles As Potential Nanocatalysts

Pd-Co Nanoalloys Nested On Cuo Nanosheets For Efficient Electrocatalytic N-2 Reduction And Room-Temperature Suzuki-Miyaura Coupling Reaction

Pentacoordinate Al 3+ Sites Anchoring Synthesis of Palladium Intermetallic Catalysts on Al 2 O 3 Supports

Pentacoordinate Al3+ Sites Anchoring Synthesis of Palladium Intermetallic Catalysts on Al2O3 Supports

A Recyclable Self-Supported Nanoporous PdCu Heterogeneous Catalyst for Aqueous Suzuki-Miyaura Cross-Coupling.

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

ChemInform Abstract: A Facile Preparation of Palladium Nanoparticles Supported on Magnetite/s‐Graphene and Their Catalytic Application in Suzuki—Miyaura Reaction.

A highly controllable, effective, and recyclable magnetic-nanoparticle-supported palladium catalyst for the Suzuki-Miyaura cross-coupling reaction

Bimetallic Pd-Cu nanocrystals and their tunable catalytic properties.

One-Step Synthesis of PdCu@Ti3C2 with High Catalytic Activity in the Suzuki-Miyaura Coupling Reaction

Ultrasonic-assisted Synthesis of Pd–Ni Alloy Catalysts Supported on Multi-Walled Carbon Nanotubes for Formic Acid Electrooxidation

Heteroepitaxial Growth of High-Index-Faceted Palladium Nanoshells and Their Catalytic Performance

Colloidal noble-metal and bimetallic alloy nanocrystals: a general synthetic method and their catalytic hydrogenation properties.

Ni/Pd core/shell nanoparticles supported on graphene as a highly active and reusable catalyst for Suzuki-Miyaura cross-coupling reaction

Palladium Nanoparticles on Assorted Nanostructured Supports: Applications for Suzuki, Heck, and Sonogashira Cross-Coupling Reactions