Abstract:This paper describes a solution-phase synthesis of high-quality vanadium dioxide thermochromic thin films. The films obtained showed excellent visible transparency and a large change in transmittance at near-infrared (NIR) wavelengths before and after the metal-insulator phase transition (MIPT). For a 59 nm thick single-layer VO(2) thin film, the integral values of visible transmittance (T(int)) for metallic (M) and semiconductive (S) states were 54.1% and 49.1%, respectively, while the NIR switching efficiencies (DeltaT) were as high as 50% at 2000 nm. Thinner films can provide much higher transmittance of visible light, but they suffer from an attenuation of the switching efficiency in the near-infrared region. By varying the film thickness, ultrahigh T(int) values of 75.2% and 75.7% for the M and S states, respectively, were obtained, while the DeltaT at 2000 nm remained high. These results represent the best data for VO(2) to date. Thicker films in an optimized range can give enhanced NIR switching efficiencies and excellent NIR blocking abilities; in a particularly impressive experiment, one film provided near-zero NIR transmittance in the switched state. The thickness-dependent performance suggests that VO(2) will be of great use in the objective-specific applications. The reflectance and emissivity at the wavelength range of 2.5-25 microm before and after the MIPT were dependent on the film thickness; large contrasts were observed for relatively thick films. This work also showed that the MIPT temperature can be reduced simply by selecting the annealing temperature that induces local nonstoichiometry; a MIPT temperature as low as 42.7 degrees C was obtained by annealing the film at 440 degrees C. These properties (the high visible transmittance, the large change in infrared transmittance, and the near room-temperature MIPT) suggest that the current method is a landmark in the development of this interesting material toward applications in energy-saving smart windows.

Synthesis and Thermochromic Properties of Vanadium Dioxide Colloidal Particles

Thermal-stimulated Phase Transition of Vanadium Dioxide Enabling Versatile Transduction and Smart Applications

Preparation and Thermochromic Property of Tungsten-Doped Vanadium Dioxide Particles

Preparation and Thermochromic Properties of Sol-Gel-derived Zr-doped VO 2 Films

Thermochromic VO2 thin films: solution-based processing, improved optical properties, and lowered phase transformation temperature

Vanadium Oxide Nanoparticles Doped Polymer to Modulate Thermal Emissivity

Optical Switching and Nanothermochromic Studies of VO2(M) Nanoparticles Prepared by Mild Thermolysis Method

The Effect of Additives on the Hydrothermal Synthesis and Thermochromic Performance of Monoclinic Vanadium Dioxide Powder

Synthesis, structure and properties of printable W-doped thermochromic VO2 with a low phase transition temperature

One-pot Hydrothermal Synthesis of Vanadium Dioxide Nanoparticles

A low-temperature synthesis of strongly thermochromic W and Sr co-doped VO2 films with a low transition temperature

Tuning Phase Transition and Thermochromic Properties of Vanadium Dioxide Thin Films via Cobalt Doping.

Facile Fabrication of Composite Vanadium Oxide Thin Films with Enhanced Thermochromic Properties

Optical properties of vanadium dioxide thin film in nanoparticle structure

One-Step Hydrothermal Synthesis, Thermochromic and Infrared Camouflage Properties of Vanadium Dioxide Nanorods

Synthesis of vanadium dioxide thin films and nanostructures

A convenient method to fabricate sputtered thermochromic VO2 nanoparticles by SiO2 microspheres for smart windows

One-step ball milling synthesis of VO2 (M) nanoparticles with exemplary thermochromic performance

Fabrication of vanadium dioxide thin films and application of its thermochromic and photochromic nature in self-cleaning: A review

Enhanced Thermochromic Performance of VO2 Nanoparticles by Quenching Process

Optical and electrical properties of vanadium oxides synthesized from alkoxides