Application of Four Ionic Liquids As Plasticizers for Pvc Paste Resin

Sui Wang,Linxi Hou
IF: 2.485
2011-01-01
Iranian Polymer Journal
Abstract:VC paste resin is an important poly(vinyl chloride) product which is applied in artificial leather fabrication, film applicator coatings and medical catheters' production. To make products flexible or just avoid adopting the debated phthalates as plasticizers, four kinds of room temperature ionic liquids (ILs), [omim]PF 6 (1-octyl-3-methylimidazolium hexafluorophosphate), [bupy]PF 6 (1-butyl-pyridine hexafluorophosphate), [C 14 mim]Br (1-tetradecyl -3-methylimidazolium bromide) and [C 16 mim]Br (1-hexadecyl -3-methylimidazolium bromide) were used as plasticizers for PVC paste resin, respectively. The mechanical properties, thermal and photo stabilities of plasticized PVC film samples were investigated by universal testing machine and TG/DTA methods. The results showed that the glass transition temperature (T g ) of 20 wt% of a plasticized sample is lower than that of an unplasticized sample. By increasing plasticizer dosages from 10 wt% to 40 wt%, the tensile strength and elastic modulus of the polymer decreased gradually though its elongation-at-break increased distinctly. The high temperature stability experiments showed that the decomposition temperature and mass loss depend intensively on the composition and structure of the ionic liquids. However, they were slightly affected by the plasticizer content. Moreover, the elongation-at-break measured data proved that ionic liquid-plasticized PVC films display reasonable UV-stability.
What problem does this paper attempt to address?