Abstract:In this work, ammonium polyphosphate (APP) was surface-modified by bio-based arginine (Arg) for the first time to enhance its flame retardance for fire-safety epoxy resin (EP). The structure of Arg modified APP (Arg-APP) was characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), 1H nuclear magnetic resonance (1H-NMR), and scanning electron microscopy (SEM). The results illustrated that Arg was attached on the surface of APP through a cation exchange reaction. With Arg acting as the efficient carbon source, the char-forming ability of Arg-APP was significantly improved as illustrated by thermogravimetric analysis (TGA). The flame retardance of EP/APP and EP/Arg-APP composites was evaluated using the limit oxygen index (LOI), vertical burning tests (UL-94), and cone calorimeter tests (CCT). The results showed that at the same weight loading (15 wt%), Arg-APP had better flame retardance and smoke suppression performance compared with pristine APP, which can be attributed to Arg-APP constituting an integrated intumescent flame retardant (IFR) and facilitating formation of char residues with significantly expanded structures and higher carbonization degrees. When the weight loading of Arg-APP reached 25 wt%, the EP/Arg-APP composite could achieve an LOI value as high as 34.7%, pass V-0 requirements in UL-94 tests, and decrease the peak heat release rate and total smoke production by 83.5% and 61.1% compared with neat EP in CCT, respectively, indicating the superior flame retardance performance of Arg-APP. Finally, the effects of the flame retardant additives on the mechanical properties of EP were evaluated by the differential scanning calorimetry (DSC) tests and tensile-strain tests. At the same additive weight loading (15 wt%), the EP/Arg-APP composite showed higher glass-transition temperature and better tensile-strain properties compared with EP/APP composite, which can be attributed to the Arg shell structure improving the compatibility between APP and the organic substrate. In conclusion, this work presents a convenient and environmentally friendly method to improve the practical performance of APP.

Kinetic Study on Surface Modification of Ammonium Polyphosphate with Melamine

Modified Ammonium Polyphosphate and Its Application on Polypropylene

Analysis of Kinetics of Thermal Decomposition of Melamine Blended with Phosphorous Ionic Liquid by Green Approach

Surface modification of ammonium polyphosphate by supramolecular assembly for enhancing fire safety properties of polypropylene

Influence of modified ammonium polyphosphate on the fire behavior and mechanical properties of polyformaldehyde

Melamine-containing polyphosphazene wrapped ammonium polyphosphate: A novel multifunctional organic-inorganic hybrid flame retardant

Microencapsulation of Ammonium Polyphosphate: Preparation, Characterization, and Its Flame Retardance in Polypropylene

Synthesis of a Novel Intumescent Flame Retardant and Its Flame Retardancy in Polypropylene

A Schiff Base-Coated Ammonia Polyphosphate for Improving Thermal and Fire-Retardant Properties of Unsaturated Polyester

Flame Retardancy and Thermal Properties of Epoxy Composite Containing Ammonium Polyphosphate

Surface modification on ammonium polyphosphate and its enhanced flame retardancy in thermoplastic polyurethane

Microencapsulated Ammonium Polyphosphate with Urea–melamine–formaldehyde Shell: Preparation, Characterization, and Its Flame Retardance in Polypropylene

Preparation of melamine–formaldehyde resin-microencapsulated ammonium polyphosphate and its application in flame retardant rigid polyurethane foam composites

Microencapsulated Ammonium Polyphosphate with Glycidyl Methacrylate Shell: Application to Flame Retardant Epoxy Resin

Synergistic Flame Retardant Effect of Melamine in Ethylene–vinyl Acetate/layered Double Hydroxides Composites

Bio-based arginine surface-modified ammonium polyphosphate: an efficient intumescent flame retardant for epoxy resin

Preparation and Characterization of Double Shell Microencapsulated Ammonium Polyphosphate and Its Flame Retardance in Polypropylene

Recent Advances in Constructing New Type of Epoxy Resin Flame Retardant System Using Ammonium Polyphosphate

Integration of safety and energy storage: Experimental study on thermal and flame-retardant properties of ammonium polyphosphate/polyvinyl alcohol/modified melamine foam as a composite phase change material

Highly efficient replacement of traditional intumescent flame retardants in polypropylene by manganese ions doped melamine phytate nanosheets

Microencapsulation of Ammonium Polyphosphate with PVA–melamine–formaldehyde Resin and Its Flame Retardance in Polypropylene