Abstract:Commercial silica support pellets were impregnated and calcined to contain cobalt oxide and ruthenium oxide for Fischer-Tropsch synthesis (FTS). The precatalyst pellets were split evenly into two groups, the control precatalyst (c-precat) and silylated precatalyst (s-precat), which were treated with 1H,1H, 2H, 2H-perfluorooctyltriethoxysilane (PFOS) in toluene. The samples of powderized s-precat were superhydrophobic, as determined by the water droplet contact angle (>150°) and sliding angle (<1°). Thermal analysis revealed the PFOS groups to be thermally stable up to 400 °C and temperature programmed reduction (TPR) studies showed that H2 reduction of the cobalt oxide to cobalt was enhanced at lower temperatures relative to the untreated c-precat. The two active catalysts were examined for their FTS performance in a tubular fixed-bed reactor after in situ reduction at 400 °C for 16 h in flowing H2 to give the active catalysts c-cat and s-cat. The FTS runs were performed under identical conditions (255 °C, 2.1 MPa, H2/CO = 2.0, gas hourly space velocity (GHSV) 510 h–1) for 5 days. Each catalyst was examined in three runs (n = 3) and the mean values with error data are reported. S-cat showed a higher selectivity for C5+ products (64 vs. 54%) and lower selectivity for CH4 (11 vs. 17%), CO2 (2 % vs. 4 %), and olefins (8% vs. 15%) than c-cat. S-cat also showed higher CO conversion, at 37% compared to 26%, leading to a 64% increase in the C5+ productivity measured as g C5+ products per g catalyst per hour. An analysis of the temperature differential between the catalyst bed and external furnace temperature showed that s-cat was substantially more active (DTinitial = 29 °C) and stable over the 5-day run (DTfinal = 22 °C), whereas the attenuated activity of c-cat (DTinitial = 16 °C) decayed steadily over 3 days until it was barely active (DTfinal < 5 °C). A post-run surface analysis of s-cat revealed no change in the water contact angle or sliding angle, indicating that the FTS operation did not degrade the PFOS surface treatment.

Superhydrophobic materials as efficient catalysts for hydrocarbon selective oxidation.

The Effect of Hydrophobically Modified Iron Catalysts with Hexadecyltrimethoxysilane on Fischer‐Tropsch Synthesis

Engineering the core shell structure CoMnOx@OTS cubic catalyst with excellent water resistant for low-temperature catalytic combustion of VOCs

Superhydrophobic Surface Modification of a Co-Ru/SiO2 Catalyst for Enhanced Fischer-Tropsch Synthesis

Unveiling the Water-Resistant Mechanism of Cu(I)-O-Co Interfaces for Catalytic Oxidation

Synthesis and Characterization of Superhydrophobic Epoxy Resin Coating with SiO2@CuO/HDTMS for Enhanced Self-Cleaning, Photocatalytic, and Corrosion-Resistant Properties

Enhanced Activity and Water Resistance on CuO/SiO2-TiO2 Catalyst for CO Oxidation and NO Reduction by CO: The Promotion Effect of SiO2

Chitosan –NH2 derived efficient Co3O4 catalyst for styrene catalytic oxidation: Simultaneously regulating particle size and Co valence

Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes

Functional and versatile superhydrophobic coatings via stoichiometric silanization

Super-hydrophobic Fluorination Mesoporous MCF/TiO2 Composite As a High-Performance Photocatalyst

Fabrication of superhydrophobic surfaces with hierarchical structure and their corrosion resistance and self-cleaning properties

Superhydrophobicity : ConstructingHomogeneous CatalystsintoSuperhydrophobicPorousFrameworks to Protect Them Fromhydrolyticdegradation

Bioinspired spiderweb-liked protective hydrophobic layer for improving the durability of superhydrophilic/air superoleophobic coatings

Hydrophobic Modification of Microenvironment of Highly Dispersed Co3O4 Nanoparticles for the Catalytic Selective Oxidation of Ethylbenzene

Ultrafine platinum/iron oxide nanoconjugates confined in silica nanoshells for highly durable catalytic oxidation

Highly Selective Α-Mn2o3 Catalyst for Cgpf Soot Oxidation: Surface Activated Oxygen Enhancement Via Selective Dissolution

Fabrication of Super-Hydrophobic Titanosilicate Sub-micro Sphere with Enhanced Epoxidation Catalytic Activity

Facile Fabrication of Robust, Multi-Functional and Superhydrophobic Coatings with Corrosion Resistance and Anti-Icing Performance

Interfacial CoOx Layers on TiO2 As an Efficient Catalyst for Solvent-Free Aerobic Oxidation of Hydrocarbons.

Superhydrophobic materials with good oil/water separation and self-cleaning property