Abstract:Degumming, chemical oxidation, and surface modification processes of carbon fibers (CFs), and printing of CF/photopolymer composites. Light‐curing rapid prototyping (SLA) has become an emerging technology in the manufacturing industry because of its high precision, rapid prototyping, and the ability to mold complex parts. To enhance the mechanical properties and thermal stability of its raw material photosensitive resin (PR), carbon fiber (CF) was surface modified by chemical oxidation and grafting of amino silane (KH550) to obtain KH550‐modified carbon fiber (ACF). Then, ACF was composited with photosensitive resin to obtain modified carbon fiber/photosensitive resin (ACF/PR) composites. The viscosities of ACF/PR composites, including the viscosity, curing shrinkage, mechanical properties, and thermal stability of the ACF/PR composites, were characterized. The results showed that KH550 was successfully grafted onto CF. When the addition of ACF in the composites was 0.6%, the tensile strength, elongation at break, and impact strength of ACF/PR reached 39.48 MPa, 20.32%, and 13.62 kJ/m2, which were 120%, 27.15%, and 154% higher than that of the pure resin; the thermal decomposition temperatures and the maximum thermal decomposition temperatures at 50% mass loss of ACF/PR increased to 457.66°C and 442.44°C at 50% mass loss, which is 3.95% and 3.63% higher than that of the pure resin. Currently, the composites have excellent strength, toughness, and thermal stability. This paper gives a cost‐efficient method for improving the functioning of PR. Highlights Mixed acid oxidation and amino silane modification of CFs. Preparation of modified CF/photosensitive resin composites. Composites with excellent mechanical properties and thermal stability.

Preparation of Acidic Resin-Carbon Composite Material Through the Sulfonation and Carbonization of Polyphenyl

Soft-template synthesis of sulfonated mesoporous carbon with high catalytic activity for biodiesel production

Sulfonated Carbon Materials with Hydrophilic and Lipophilic Properties

Preparation of a Novel Sulfonated Carbon Catalyst for the Etherification of Isopentene with Methanol to Produce Tert-Amyl Methyl Ether

Preparation of Expanded Graphite-based Carbon/Carbon Composites and Its Adsorption Properties on Phenol

Enhancement of interfacial properties of carbon fiber reinforced polyphenylene sulfide resin by sulfur treatment

Preparation of acidic Fe-SiO2 catalyst and its catalytic reactivity in photo-Fenton reaction

Loading behavior of p-toluenesulfonic acid in biochar and its application to prepare 5-hydroxymethylfurfural

Selective Synthesis of Bisphenol F from Phenol and PODE2 over an Acidic Resin–Carbon Composite Material

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

High-Yield Preparation and Properties of Phenolic Resin-Based Carbon Microspheres

Sulfonic polymer catalysts for converting of furfural to high-value chemicals

Sulfonated sucrose-derived carbon: Efficient carbocatalysts for ester hydrolysis

Preparation of Activated Carbon-Based Solid Sulfonic Acid and Its Catalytic Performance in Biodiesel Preparation

Ph-SO3H-modified Mesoporous Carbon As an Efficient Catalyst for the Esterification of Oleic Acid

Improving carbon fibre reinforced polyphenylene sulfide using amine and phenolic interphase modifications

Preparation and structure analysis of carbon/carbon composite made from phenolic resin impregnation into exfoliated graphite

Preparation of Sulfo-Group-Bearing Mesoporous-Silica-Based Solid Acid Catalyst and Its Application to Direct Saccharification

Preparation of short carbon fiber reinforced photosensitive resin and composite material properties study

Catalytic Conversion of Fructose to 5-Hydroxymethylfurfural by a Novel Sulfonated Carbonaceous Material

Preparation and Properties of Multi-Walled Carbon Nanotube/carbon/polystyrene Composites