Iodine‐ion‐induced Size‐tunable Co3O4 Nanowires and the Size‐dependent Catalytic Performance for CO Oxidation
Yaguang Li,Liping Zhu,Yanmin Guo,Jie Jiang,Liang Hu,Zhen Wen,Luwei Sun,Zhizhen Ye
DOI: https://doi.org/10.1002/cctc.201300444
IF: 4.5
2013-01-01
ChemCatChem
Abstract:CO oxidation is one of the most important catalytic reactions owing primarily to its relevance in practical applications in carexhaust emission control, fuel cells, and air purification. Meanwhile, scientifically, it is one of the simplest catalytic reactions and thus is widely used as a model system to understand heterogeneous catalysis. Gold nanoparticles deposited on various metal oxides that show high activity for CO oxidation have aroused tremendous interest since Haruta et al. reported that gold nanoparticles show high activity for CO oxidation. Owing to the high cost of gold-based catalysts, other alternatives would be highly desirable. As an alternative, Co3O4 has been also been considered as a catalyst for CO oxidation. 13, 18, 19] Many groups have tried to control the shape of the catalyst to obtain higher catalytic efficiency, since the activity for CO oxidation strongly depends on the exposed specific crystal planes. 19] Moreover, several groups have synthesized small Co3O4 nanoparticles that displayed much higher catalytic activity, 18] even though there are no specific active planes on the surface of their Co3O4 nanostructures. For instance, Sch th et al. reported small Co3O4 nanoparticles without exposed specific active planes that have much higher activity for CO oxidation than the bulk materials. However, size-dependent chemistry of Co3O4 for catalytic oxidation of CO has been rarely investigated, owing to the uncontrollable size of the Co3O4 nanostructures. In this work, we present a novel synthesis method, which adopts the iodine ions (I ) for the formation of size-tunable Co3O4 nanowires. This method can not only regulate the diameter of nanowires in a wide range from 17 to 150 nm, but also build up a dandelion-like hierarchical structure rapidly. It is observed that I ions played a key role in tuning the dimension of nanowire and promoting the formation of the complex nanostructures. The thinner Co3O4 nanowires with diameter of 15 nm have ultrahigh conversion rate for CO oxidation, which is estimated to be 772 mmol gcat 1 s 1 at 180 8C, and the catalytic performance depends on the size of nanowires. We studied the kinetics of the catalytic reaction of Co3O4 nanowires with different size, which was consistent with the Raman and temperature-programmed desorption curves of oxygen (O2-TPD) experiments. Our results indicate that the major reason of the ultrahigh CO oxidation rate for small size Co3O4 nanowires is the large numbers of weakly bonding oxygen ions on surface edges. So the iodine ions induced synthesis method can directly contribute to improving catalytic performance by controlling the size of nanowires. Shown in Figure 1 are the as-synthesized Co(CO3)0.5(OH)·0.11 H2O nanowires with the addition of NaI. The crystal phase of the as-synthesized product is determined by X-ray diffraction (XRD), with the result shown in Figure 1 a. All the identified peaks can be assigned to pure orthorhombic Co(CO3)0.5(OH)·0.11 H2O. [20] It is clear from the panoramic view (Figure 1 b) that the Co(CO3)0.5(OH)·0.11 H2O nanowires comprise an uniform dandelion-like microsphere and the nanowires are uniform with 4 mm in length. Such a 1 D nanostructure is also revealed under transmission electron microscope (TEM). Under a higher magnification, these nanowires are shown to have a needle-like structure along the axial direction, and the diameter is approximately 17 nm with a smooth surface (Figure 1 c). The exposed crystal surfaces of the nanowires are (0 1 0) and (0 0 1) planes grown along the [1 0 0] direction (Figure 1 d, 1 e). Interestingly, when the samples are synthesized in the absence of NaI, the Co(CO3)0.5(OH)·0.11 H2O nanowires could still be generated with the diameters of 130 nm (Supporting Information, Figure S1 e). Moreover, their arrangement is disordered and the dandelion-like microspheres no longer form (Supporting Information, Figure S1 a). Several template-free methods have been successfully applied to synthesize self-assembled structures of materials. However, to be able to synthesize complex nanostructures of cobalt-based materials, generally high temperature and especially long reaction times are needed. 24, 27] It was, therefore, necessary to develop a simple and effective method that could to synthesize complex cobalt-based nanostructures on a largescale in a short time. In our strategy, the formation of self-assembled Co(CO3)0.5(OH)·0.11 H2O structures is faster and strongly depends on the presence of I ions. Shown in Scheme 1 are the differences between the traditional process and I ions induced self-assembled process and describes how I ions can change the evolution processes to make the growth faster. In the self-assembled evolution reported previously, 27] recrystallization plays a pivotal role in the formation of individual nanocomponents and lateral fusion drives the aggregation of individual nanocomponents in an orderly fashion in the presence [a] Y. Li, Prof. Dr. L. Zhu, Y. Guo, Dr. J. Jiang, L. Hu, Z. Wen, Dr. L. Sun, Prof. Dr. Z. Ye State Key Laboratory of Silicon Materials Department of Materials Science and Engineering Zhejiang University Hangzhou 310027 (P.R. China) Fax: (+ 86) 571-87952625 E-mail : zlp1@zju.edu.cn [b] Y. Li, Prof. Dr. L. Zhu, Y. Guo, Dr. J. Jiang, L. Hu, Z. Wen, Dr. L. Sun, Prof. Dr. Z. Ye Cyrus Tang Center for Sensor Materials and Applications Zhejiang University Hangzhou 310027 (P.R. China) Supporting information for this article is available on the WWW under http://dx.doi.org/10.1002/cctc.201300444.