POLYMERIZATION, STRUCTURES AND THERMAL PROPERTIES OF PHOSPHAPHENANTHRENE-CONTAINING POLY(1-PENTYNE)

Yang Fan,Tong Bin,Shi Jianbing,Zhi Junge,Shen Jinbo,Dong Yuping

DOI: https://doi.org/10.3724/sp.j.1105.2011.11111

2011-01-01

Acta Polymerica Sinica

Abstract:The phosphaphenanthrene-containing 1-pentyne monomer (M-34) was synthesized through the successive esterification of 2-(6-oxide-6H-dibenz < c, e > < 1, 2 > oxaphos-phorin-6-yl)-dihydroxyphenylene (ODOPB) with 4-(4-pentynoxy)benzoyl and 4-butyloxybenzoyl, respectively. Due to the introduction of 9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide (DOPO) group, the catalytic ability of Rh-based catalysts ([Rh(nbd) Cl](2) and Rh (nbd) B(C-6 H-5)(4)) is decreased and the yields of polymer are relatively low. The polymerization of model monomer (M-0) in the absence of phosphaphenanthrene side-group was, however, carried out in high yield at the same condition. The microstructure of the poly (1-pentyne) derivants was characterized by means of H-1-NMR. The experimental results indicate that the main-chains of poly(1-pentyne) derivants with high trans-content configuration are produced due to the strong pi-pi stacking and polar interactions between phosphaphenanthrene-containing pendent groups. Thus, the interaction between adjacent pendent groups is further strengthened. The molecular weights and distribution of P-34 and its model polymer P-0 were measured by GPC; Their thermal properties were evaluated by TGA and DSC. Comparing with P-0 in the absence of phosphaphenanthrene side-group,TGA analysis reveals the excellent thermal stability of P-34, losing 1% of weights during heating to 270 degrees C and retaining 50% of weights after pyrolyzis at 550 degrees C. And the char yield of P-34 is over 50 wt% at 550 degrees C. The DSC results indicate that T-g of P-34 is lower than that of P-0 because DOPO increases the volume of side-groups in P-34.