Biosynthesis of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) in metabolically recombinant Escherichia coli
Changfeng Miao,Dong Meng,Yuling Liu,Fang Wang,Lu Chen,Zhaosong Huang,Xiangyu Fan,Pengfei Gu,Qiang Li
DOI: https://doi.org/10.1016/j.ijbiomac.2021.10.183
IF: 8.2
2021-12-01
International Journal of Biological Macromolecules
Abstract:In this study, a phaC<sub>R</sub> gene encoding PHA synthase was identified in Rhodoligotrophos defluvii which was adjacent to β-ketothiolase encoded by phaA<sub>R</sub> gene and acetoacetyl-CoA reductase encoded by phaB<sub>R</sub> gene. Amino acid comparison of PhaC<sub>R</sub> showed the highest homology of 65.98% with PhaC of R. appendicifer, while its homology with typical class I PHA synthase in Cupriavidus necator was only 42.54%. PHA synthesis genes were then transformed into E. coli harboring phaCAB<sub>R</sub> and phaC<sub>R</sub>AB<sub>C</sub> which were cultured with 15 g/L glucose respectively, and 20.46 wt% and 16.95 wt% of CDW for poly(3-hydroxybutyrate) (PHB) were accumulated respectively. To further explore the effect of substrate specificity for PHA production, the ptsG gene was then deleted and 15 g/L glucose and 1.5 g/L propionate were co-employed as carbon sources, which enabled the synthesis of poly(3HB-co-3HV) copolymer. As a result, poly(3HB-co-3HV) was accumulated up to 24.74 wt% of CDW, and the highest content of 3-hydroxyvalerate (3HV) was 10.86 mol%. The T<sub>d5</sub> was 260 °C, which implied that it possessed good thermal stability, and the M<sub>w</sub> of GPC in recombinant strains were between 22 and 26 × 10<sup>4</sup> g/mol, and the highest PDI was 3.771. The structure of poly (3HB-co-3HV) copolymer was determined through <sup>1</sup>H NMR analysis.
polymer science,biochemistry & molecular biology,chemistry, applied