Abstract:Mullite whiskers were prepared using molten salt reaction. The resulting whiskers have been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TG-DSC) and high resolution transmission electron microscopy (HRTEM). SEM studies showed that diameter of the mullite whiskers was in a range of 200 similar to 400 nm and their length was several microns. The analysis of HRTEM data revealed that the interplanar spacing was 0.539 nm, in accordance with the spacing of (110) crystal plane of mullite. As silica species was introduced into starting reactants, the combination reaction of mullite formation took place, gamma-Al2O3 was consumed and mullite whiskers grew continuously. The most important factor in controlling mullite formation is the decomposition reaction of aluminum sulfate, and alpha-Al2O3 is fabricated by thermal pyrolysis of aluminum sulfate at 900 degrees C in molten sodium sulfate system without silica species participating. According to the thermodynamic calculation, alpha-Al2O3 is a stable phase as the product of the decomposition of Al-2 (SO4)(3) in comparison to gamma-Al2O3, and mullite formation reaction is a spontaneous process in the whole temperature range. The decomposition reaction of aluminum sulfate was investigated by Kissinger-Akahira-Suno method with various heating rates (beta=5, 10 and 15 K center dot min(-1)), and the apparent activation energy (E-a) of reaction is 257.2 kJ center dot mol(-1).

Influence of the sediment properties of Al2O3· xH2O on the hydrothermal formation alooh whiskers

Influence of the Sediment Properties of Al2O3⋅xH2Oon the Hydrothermal Formation AlOOH Whiskers

Influence of Al 2 O 3 · XH 2 O Crystallinities on the Morphology of AlOOH Whiskers

Condition Control Morphology TEM Analysis of Hydrothermal Preparation of Nanometer AlOOH Whisker

Progress in the Hydrothermal Formation of Dispersive Nano-Particles and Whiskers

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Influence of Alkyl Trimethyl Ammonium Bromides on Hydrothermal Formation of Α-Caso4·0.5h2o Whiskers with High Aspect Ratios

On the Synthesis and Dispersion of MuIIite Whiskers

Effect of pH and sulphate on the morphology of γ-AlOOH

Preparation and Characterization of Mullite Whiskers from Different Silica Sources via Molten Salt Reaction

Influence of NH4Cl on Hydrothermal Formation of Α-Caso4·0.5h2o Whiskers

Wetting of Microstructured Alumina Fabricated by Epitaxial Growth of Al 4 B 2 O 9 Whiskers

Effects of Metal Ions on the Morphology of Calcium Sulfate Hemihydrate Whiskers by Hydrothermal Method

Effect of Precursor on Aggregation of AlOOH Nano-particles Prepared by Hydrothermal Process

Synthesis and microstructural characterization of aluminum borate whiskers

Growth of Al 2 O 3 Whiskers by Vapour-Phase Reactions

Hydrothermal formation and characterization of magnesium oxysulfate whiskers

Synthesis of ZnO Whiskers Via Hydrothermal Decomposition Route

Experimental Study of Synthesizing Mullite Whiskers by Andalusite-Sericite Phyllite

Morphology Evolution in Hydrothermal Synthesis of Mesoporous Alumina

Synthesization and Crystallization Mechanism of Nano-Scale Γ-Alooh with Various Morphologies