Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Condensation Behavior of Ag Aggregates on Liquid Surfaces

Aggregation Mechanism of Ag Atoms Deposited on Liquid Surfaces

Temperature Dependence of the Aggregation Mechanism of Silver Atoms Deposited on Liquid Substrates

AGGREGATION CHARACTERISTICS OF SILVER ATOMS DEPOSITED ON LIQUID SUBSTRATES

Studies on A Nonequilibrium Atomic Cluster System with Repulsive Interactions

Nucleation, Growth, and Aggregation of Ag Clusters on Liquid Surfaces

Aggregation Behavior and Microstructure of Silver Thin Films on Ionic Liquid Substrates

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Aggregation Behavior of Au Atoms and Atomic Islands on Liquid Surfaces

Morphology and Microstructure of Ag Islands of Aggregated Atoms on Oil Surfaces

Diffusion and Aggregation Behaviors of Silver Atoms on Charged Liquid Substrates

Fractal Ag-Aggregates on Silicone Oil Surfaces

Influence of an Adsorption Layer and Its Evolvement on the Formation of Ag.

Diffusion,Coalescence and Coarsening:Evolution of Silver Clusters and Thin Films Deposited on a Liquid Surface

Preferred Structures Of The Atomic Ag Islands On Silicone Oil Surfaces

Silver Deposition on Oil – Cluster Nucleation, Growth and Aggregation on a Liquid Surface

Nucleation, Growth, And Aggregation Of Au Nanocrystals On Liquid Surfaces

Aggregation of Organic Molecules on Silver Surface with the Balance Between Molecule–substrate Interaction and Intermolecular Interaction

AFM Study on the Formation Mechanism and Microstructure of Ni Atomic Aggregates on Liquid Substrates

Experimental Observation of Large Ramified Au Aggregates on Melting Glass Surfaces

Synthesis and Characterization of Monodispersed Zns - Ag Colloids