Abstract:Nitrogenated tetrahedral amorphous carbon (ta-C : N) films were prepared on the polished C--Si substrates by introducing highly pure nitrogen gas into the cathode region and the depositing chamber synchronously using filtered cathodic vacuum arc (FCVA) technology. The nitrogen content in the films was controlled by changing the flow rate of nitrogen gas. The configuration of ta-C : N films was investigated by means of X-ray photoelectron spectroscopy (XPS) and visible Raman spectroscopy. It was shown that the nitrogen content in the films increased from 0.84 at% to 5.37 at% monotonously when the nitrogen flow rate was varied from 2 seem to 20 sccm. The peak position of C (1s) core level moved towards higher binding energy with the increase in nitrogen content. The shift of C (1s) peak position could be ascribed to the chemical bonding between carbon and nitrogen atoms even though more three-fold coordinated sp2 configuration as in graphite was formed when the films were doped with more nitrogen atoms. Additionally, the half width of C(1s) peak gradually was also broadened with increasing nitrogen content. In order to discover clearly the changing regularities of the microstructure of the films, the XPS C(1s) spectra and Raman spectra were deconvoluted using a Gaussian-Lorentzian mixed lineshape. It was shown that the tetrahedral hybridization component was still dominant even though the ratio of sp2/sp3 obtained from C(1s) spectra rose with the increase in nitrogen content. The Raman measurements demonstrated that the G peak position shifted towards higher frequency from 1,561 to 1,578 cm(-1) and the ratio of ID/IG also rose with the increase in nitrogen content. Both results indicated that the graphitizing tendency could occur with the increase in nitrogen content in the films.

Synthesis and Bonding Properties of Carbon Nanotubes with Different Nitrogen Contents

Tensile Properties of a Boron/nitrogen-Doped Carbon Nanotube–graphene Hybrid Structure

Role of Nitrogen on the Mechanical Properties of the Novel Carbon Nitride Nanothreads

Structural and Compositional Regulation of Nitrogen-Doped Carbon Nanotubes with Nitrogen-Containing Aromatic Precursors

The Preparation of Nitrogen-doped Carbon Nanotubes from Pyridine

Nitrogen Doping Effects on Microstructure of Multi-Walled Carbon Nanotubes

Ab Initio Study of Nitrogen-Doped Carbon Nanotubes

Nitrogen-doped carbon nanotubes synthesized with carbon nanotubes as catalyst

Influence of Growth Temperature on the Structure, Composition and Bonding Character of Nitrogen-Doped Multiwalled Carbon Nanotubes

Synthesis of Nitrogen-Doped Single-Walled Carbon Nanotubes and Monitoring of Doping by Raman Spectroscopy

Synthesis, Photoluminescence, and Magnetic Properties of Nitrogen-Doping Helical Carbon Nanotubes

Effect of Nitrogen Doping on the Mechanical Properties of Carbon Nanotubes

High Pressure Study of Nitrogen Doped Carbon Nanotubes Using Raman Spectroscopy and Synchrotron X-ray Diffraction

Effect of nitrogen species on electrochemical properties of N-doped carbon nanotubes derived from co-pyrolysis of low-density polyethylene and melamine

Growth of carbon nanotubes and nitrogen-doped carbon nanotubes on “carbon nanotube seeds”

Preparation and Quantitative Characterization of Nitrogen-Functionalized Multi-walled Carbon Nanotubes

Structural, morphological, and photoluminescence properties of nitrogen-doped CNTs and graphitic carbon nanostructures

Atomic configuration of nitrogen-doped single-walled carbon nanotubes

Effects Of Nitrogenation On Single-Walled Carbon Nanotubes Within Density Functional Theory

XPS and Raman Spectral Analysis of Nitrogenated Tetrahedral Amorphous Carbon(ta-C:N)Films with Different Nitrogen Content

Doped Carbon Nanotube Array with a Gradient of Nitrogen Concentration