Abstract:LaFe 11·6 Si 1·4 compounds are annealed at different high temperatures from 1323 to 1623 K. The powder X-ray diffraction patterns show that large amount of NaZn13-type phase begins to be observed in LaFe 11·6 Si 1·4 compound after being annealed at 1423 K for 5 h. In the temperature range from 1423 to 1523 K, the \(\boldsymbol{\alpha} \)-Fe and LaFeSi phases rapidly decrease to form 1:13 phase. LaFeSi phase is rarely observed in the XRD pattern in the LaFe 11·6 Si 1·4 compound annealed at 1523 K (5 h). With annealing temperature increasing to 1573 K and 1673 K, La 5 Si 3 phase is detected, and there is a certain amount of LaFeSi phase when the annealing temperature is 1673 K. The amount of impurity phases in the LaFe 11·6 Si 1·4 compound annealed by the two-stage annealing consisting of high temperature (\(\boldsymbol{>}\)1523 K) and 1523 K is larger than that of the single stage annealing at 1523 K under the same time. According to the results of different high-temperature annealing, LaFe\(_{{\bf 11{\cdot}6}-\boldsymbol{x}}\)Co\(_{\boldsymbol{x}}\)Si 1·4 (\(\boldsymbol{0{\cdot}1} \boldsymbol{\le} \boldsymbol{x} \boldsymbol{\le} \boldsymbol{0{\cdot}8}\)) compounds are annealed at 1523 K (5 h). The main phase is NaZn13-type phase, and the impurity phase is a small amount of \(\boldsymbol{\alpha} \)-Fe in LaFe\(_{{\bf 11{\cdot}6}-\boldsymbol{x}}\)Co\(_{\boldsymbol{x}}\)Si 1·4 compounds. With increase in Co content from \(\boldsymbol{x} \boldsymbol{=} \boldsymbol{0{\cdot}1}\) to \(\boldsymbol{0{\cdot}8}\), the Curie temperature \(\boldsymbol{T}_{\!\boldsymbol{\rm C}}\), goes up from 207 to 285 K. The introduction of Co element weakens the itinerant electron metamagnetic transition, and also results in the change of magnetic transition type from first to second order at about \(\boldsymbol{x = 0{\cdot}5}\). The magnetic entropy change decreases from 19·94 to 4·57 J /kg K with increasing Co concentration at a low magnetic field of 0–2 T. But the magnetic hysteresis loss around \(\boldsymbol{T}_{\!\boldsymbol{\rm C}}\) reduces remarkably from 26·2 J /kg for \(\boldsymbol{x = 0{\cdot}1}\) to 0 J /kg for \(\boldsymbol{x} \boldsymbol{=} \bf 0{\cdot}8\).

The Study on the Microstructure and the Magnetocaloric Effects in LaFe10.8Co0.7Si1.5C0.2 Compound at Different Annealing Times

Microstructure and magnetic property of LaFe11.6Si1.4 magnetocaloric alloys by a novel short time heat treatment

Microstructure evolution and large magnetocaloric effect of La0.8Ce0.2(Fe0.95Co0.05)(11.8)Si-1.2 alloy prepared by strip-casting and annealing

Effect of Annealing on the Microstructure and Magnetic Properties of Fe-based Nanocomposite Materials

Structure and Magnetic Properties of Shortly High Temperature Annealing LaFe11.6Si1.4 Compound

The studies of high-temperature and short-time annealing, phase transition process, and magnetic property for LaFe 11.7Si 1.3 compound

Microstructure, Phase Evolution and Magnetocaloric Properties of LaFe11.6Si1.4/La70Co30 Composite

Phase constitution, microstructure evolution and magnetocaloric properties of LaFe<sub>11.8</sub>Si<sub>1.2</sub> strip-casting flakes

The effect of high-temperature annealing on LaFe11.5Si1.5 and the magneto- caloric properties of La1−xCexFe11.5Si1.5 compounds

The effect of high-temperature annealing on LaFe<sub>11.5</sub>Si<sub>1.5</sub> and the magnetocaloric properties of La<sub>1−<i>x</i></sub>Ce<sub><i>x</i></sub>Fe<sub>11.5</sub>Si<sub>1.5</sub> compounds

The Effect of Different Temperature Annealing on Phase Relation of LaFe11.5Si1.5 and the Magnetocaloric Effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 Alloys

Reduced Annealing Time and Enhanced Magnetocaloric Effect of La(Fe, Al) 13 Alloy by La-nonstoichiometry and Si-doping

The influence of different cooling processes on phase, microstructure, and magnetocaloric properties of LaFe 11.6 Si 1.4 compounds

Study of Magnetocaloric Effect in LaFe11.5Si1.5 Alloys Prepared by Different Cooling Methods

Phase Relation of LaFe 11·6 Si 1·4 Compounds Annealed at Different High-Temperature and the Magnetic Property of LaFe 11·6– X Co X Si 1·4 Compounds

Effect of annealing on microstructure and magnetocaloric properties of plastically deformed La0.7Ce0.3Fe13.68Mn0.2Si1.4 alloys

Microstructure, Magnetocaloric and Mechanical Properties of LaFe 11.8 Si 1.2 /Y 64 Co 36 Composites Prepared by Hot Pressing and Diffusion Annealing

Structure and Magnetic Properties of LaFe11.5−xCoxSi1.5C0.2 Compounds for Magnetic Refrigeration Near Room Temperature

The Study of Phase, Microstructure, and Magnetocaloric Properties in LaFe11.6*xSi1.4B0.1alloys

Phase, Microstructure, and Magnetocaloric Effect of the Large Disc LaFe11.6Si1.4 Alloy

Change of Microstructure and Magnetic Properties of Sintered Nd–Fe–B Induced by Annealing