Magnetic Properties of Perpendicularly Orientated L1(0) Fept Nanoparticles

Mo XiaoJing,Xiang Hui,Li GuoQing,Chen Peng,Xiong ZuHong,Wang JunZhong,Ishio ShunJi,Saito Hitoshi,Shima ToshiYuki,Takanashi Koki
DOI: https://doi.org/10.1007/s11434-010-0077-7
2010-01-01
Chinese Science Bulletin
Abstract:L1(0) FePt films were deposited on MgO (001) substrates heated to 700A degrees C by magnetron sputtering. Assisted by the misfit of lattice between film and substrate, strong (001) texture was formed. The film at nominal thickness t (N) = 5 nm was composed of nanoparticles with a size of similar to 70 nm, and showed a high coercivity of similar to 105 kOe at 4.2 K. At t (N) =similar to 50 nm, as the film changed from discontinuous to continuous, the coercivity dropped about one order of magnitude. Micromagnetic simulation implies that the magnetization reversal is a vortex-like nuclear type. The ideal coercivity of a separated single-domain L1(0) FePt nanoparticle with a size of 70 nmx 70 nmx 5 nm is similar to 121 kOe. This tells us that the experimental coercivity has nearly reached the limit of ideal single crystalline nanoparticles.
What problem does this paper attempt to address?