Investigation of magneto-electric properties of Co0.65Zn0.35Fe2O4–Ba0.7Sr0.3TiO3 multiferroic composites
Hanamanta Badiger,Shantinath Latthe,Shidaling Matteppanavar,Nandakumar Kalarikkal,B. G. Hegde
DOI: https://doi.org/10.1007/s10854-024-13062-w
2024-07-26
Journal of Materials Science Materials in Electronics
Abstract:Ferromagnetic Co 0.65 Zn 0.35 Fe 2 O 4 (CZFO) nanoparticles were sandwiched with bulk ferroelectric Ba 0.7 Sr 0.3 TiO 3 (BSTO) material to study the magneto-electric coupling of composite system. In the present study, the CZFO nanoparticle is synthesized through sol–gel combustion and BSTO through solid-state reaction; followed by this, the composite system (1 − Φ) BSTO–ΦCZFO (Φ = 0.1, 0.2, and 0.3) was prepared by mixing according to weight percentage (Wt%) by solid-state reaction. The obtained XRD spectra of each CZFO, BSTO, and composites reflect the spinel cubic structure with space group Fd -3 m, tetragonal structure with space group P4mm, and mixed index, respectively. Utilizing Rietveld refinement process, the structural parameters are extracted. The microstructural analysis by FESEM unveiled a high porous nature characterized by a thick-walled plant cell-like structure for all the composites. The magnetic hysteresis loops show the ferromagnetic nature of CZFO and composite samples. As the content of CZFO in the BSTO composite, the magnetic saturation increases with decrease in the coercive field values, which indicates that the ferromagnetic domain is controlled by ferroelectric domain. This is indirect evidence for existence of ME coupling. The room-temperature dielectric measurement suggest that as the CZFO content increased, their dielectric constant decreased and followed a trend of Maxwell–Wagner-type polarization as obeyed with Koop's principle. Impedance study shows relaxation peaks, indicative of Debye-type polarization. The Cole–Cole plot is aligned with a semi-arc pattern and demonstrated a decrease in the radius of the semi arc as the CZFO content is mixed with BSTO and fitting well with the capacitance–resistance model. Significantly, the composition of Φ = 0.3 exhibited a ME voltage coefficient of 14.58 mV/cm Oe, which exceeded the values reported in previous research. This study reports the successful synthesis, and electrical, magnetic, and ME coupling parameters of CZFO–BSTO composites for potential applications.
materials science, multidisciplinary,engineering, electrical & electronic,physics, applied, condensed matter