Abstract:SUS430 stainless-steel/La0.8 Sr0.2 FeO3(SUS430/LSF) bilayer samples were prepared by a powder metallurgy process,using SUS430 stainless-steel powder and La0.8 Sr0.2 FeO3(LSF) powder as raw materials.Density and phase structure of the sintered SUS430 stainless-steel and LSF samples were examined.Mass increases after oxidation were recorded to study the oxidation kinetics of SUS430 stainless-steel and SUS430/LSF bilayer materials.Area specific resistance(ASR) of SUS430 stainless-steel and SUS430/LSF bilayer material was tested by the 4-probe method.Microstructure of the materials before and after oxidation was also observed.The results show that dense LSF coating on the surface of sintered stainless-steel substrate can be obtained by this method.The LSF coating keeps tight bonding with the stainless-steel substrate after repetitive oxidation.The oxidation rate constant of SUS430/LSF bilayer material was 2.81 × 10-15 g2.cm-4.s-1 after oxidation at 800 ℃ in air for 150 h,which is more than one order of magnitude lower than that of SUS430 stainless-steel,and the ASR of SUS430/LSF bilayer material reduces from 74.65 mΩ.cm2(value of SUS430 stainless-steel sample) to 15.55 mΩ.cm2.

Development of Novel Interconnect Materials for Intermediate Temperature Solid Oxide Fuel Cell