Stabilization of Divalent Eu2+ in Fluorosilicate Glass-Ceramics Via Lattice Site Substitution
Chenhao Wang,Xiaotong Chen,Xue Luo,Junjie Zhao,Xvsheng Qiao,Yong Liu,Xianping Fan,Guodong Qian,Xianghua Zhang,Gaorong Han
DOI: https://doi.org/10.1039/c8ra06843g
IF: 4.036
2018-01-01
RSC Advances
Abstract:Fluorosilicate glasses and glass-ceramics with MF2 (M = Ca, Sr, Ba), ZnF2 or LaF3 components were investigated to host divalent Eu2+ for photoluminescence (PL) application. X-ray diffraction phase identification and a series of spectroscopic analyses were performed to reveal the relationship between microstructure and the reduction of Eu3+ → Eu2+. The precursor glasses were believed being constituted by silicate-rich phases and fluoride-rich phases, due to the immiscibility of fluoride-and-silicate mixed glass system. After heat treatment, the fluoride-rich glass phases could transform into fluoride crystalline phase in the glass-ceramics. Europium tended to enrich in the fluoride-rich phases in the glasses or in the precipitated fluoride crystalline phases in the glass-ceramics. Small amounts of Eu3+ were reduced to Eu2+ in the glasses where the electronegativity had a crucial impact. In contrast, large amounts of Eu3+ were reduced to Eu2+ in the glass-ceramics containing MF2 nanocrystals, where the reduction was determined by lattice site substitution. Using ZnAl2O4 containing glass-ceramics as reference, it was evidenced that the similar and a little larger radii between sites and substitution ions are the prerequisite for Eu3+/M2+ substitution. And using LaF3 containing glass-ceramics as reference, it was certified that unbalanced charge at substitution sites induce the Eu3+ → Eu2+ reduction.