Recovery of Indium from Hard Zinc Slag by Pressure Leaching and Solvent Extraction
Zhigan Deng,Xingbin Li,Chang Wei,Gang Fan,Minting Li,Cunxiong Li
DOI: https://doi.org/10.1007/s11837-020-04519-4
2021-01-04
JOM
Abstract:In this study, hydrometallurgical processes involving pressure acid leaching and solvent extraction were developed to aid recovery of indium from zinc slag, which is produced in the imperial smelting process. Four different acid leaching methods were studied, namely atmospheric leaching, atmospheric leaching with KMnO4, roasting-atmospheric leaching, and oxygen pressure leaching in a sulfuric acid medium. Oxygen pressure acid leaching is the most effective method for indium extraction, and 94.1% of indium was leached under the optimum conditions, i.e., 300 g/L H2SO4,oxygen pressure 0.4 MPa, liquid/solid ratio 10 mL/g, and temperature 100°C for 5 h. X-ray diffraction and scanning electron microscopy examination of the raw material and leaching residue samples indicated that the intermetallic compounds Cu5Zn8and Cu2Zn, metallic zinc, and iron in the raw material dissolved, leaving the insoluble components PbSO4 and Pb as the major compounds in the leaching residue. A 98.5% proportion of the indium in the leaching solution was selectively extracted with 30% bis(2-ethylhexyl) phosphate and 70% kerosene by three-stage counter-current extraction, and 99.5% of the indium in the loaded organic phase was stripped by 6 mol/L HCl through four-stage counter-current stripping. The overall recovery yield of indium through all processes was approximately 92%.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy