Hot Deformation Behavior and Processing Maps of PM TiAl Alloy

Hui Wang,Yong Liu,Wei Zhang,Zhou Li,Huizhong Li,Li Wang,Guangyu Yang

DOI: https://doi.org/10.3969/j.issn.0258-7076.2010.02.001

2010-01-01

Abstract:The hot deformation characteristics of PM TiAl alloy were studied in the temperature range of 1000 ～ 1150 ℃ and strain rate range of O. 001 ～ 1s~(-1) using hot compression test. The stress-strain curves exhibited an obvious peak followed by a broad flow sof-tening. In order to investigate the deformation behavior of PM TiAl alloy at a finite strain level, processing maps were constructed on the basis of a dynamic material modeling(DMM). The results showed that the alloy fall into flow instability region due to cracking at higher strain rate (> 0.1s~(-1)). Thermo mechanical processing in this region should be avoided beeanse this was harmful to deforma-tion of the alloy. Power dissipation efficiency ηranged from 35% to 50% in the temperature range of 1000 ～ 1050 ℃ and strain rate range of 0.001～0.01s~(-1). The deformation mechanism of this region was dynamic recrystallization and this region was suitable for thermo mechanical processing. When deformed at higher temperature (≥1100℃ ) and lower strain rate (0.001s~(-1)), power dissipa-tion efficiency ηreached a peak value of 60%. Superplastic deformation occurred in this region.