Abstract:A seed-mediated method was employed here for CTAB-assisted gold nanoparticle growth. 3–4 nm silver aqueous colloid was stabilized by sodium citrate and used as seed solution to initial gold particle growth. The concentration of seed solution was calculated based on its relationship with silver atom concentration and seed particle statistical mean volume. It was found that there is a maximum seed concentration of 8.57 × 10−12 M (~25 µl 0.343 × 10−8 M seed solution added) in 10 ml 2.5 × 10−4 M HAuCl4 growth solution for growth of rodlike particles. Below this seed amount, the aspect ratio of nanorods could be controlled by varying the silver seed amount, i.e. nanorods with aspect ratio ~18.9 were obtained when the seed concentration in the growth solution was 0.343 × 10−12 M by adding 1 µl 0.343 × 10−8 M silver seed solution and nanorods with aspect ratio ~9.69 were obtained when the seed concentration in the growth solution was 1.715 × 10−12 M by adding 5 µl 0.343 × 10−8 M silver seed solution. As the seed concentration in the growth solution was more than 8.58 × 10−12 M (25 µl 0.343 × 10−8 M silver seed solution was added), there were no rodlike particles formed but spherical ones instead. These spheres were further studied by TEM and found to all be hollow structures. It was suggested that there were probably two different nucleation processes for growth of nanorods and spheres. For hollow spheres, the reaction between Ag seeds and Au ions formed hollow structures based on the Ag particle template effect. Then further growth of Au on these hollow structures produced hollow gold nanospheres. For nanorods, due to the very low concentration of silver seed (molar ratio of Ag seed: Au = 3.426 × 10−8), the growth process here probably was started by silver-induced Au nucleation, in which reduction of gold ions by silver resulted in small gold clusters. These gold clusters further grew up into nanoparticles and nanorods in the presence of CTAB.

Controlling Yield and Morphology for Gold Nanorods in a Seed-Mediated Synthesis Method for Cell Imaging

Seed-mediated synthesis of silver nanocrystals with controlled sizes and shapes in droplet microreactors separated by air.

Wet chemical synthesis of gold nanoparticles using silver seeds: a shape control from nanorods to hollow spherical nanoparticles

Preparation of Gold Nanorods with Aspect Ratio 2-5 by Using Seed Mediated Growth Method

Controlled Synthesis and Cell Imaging of Gold Nanorod-Silica Core-Shell Nanoparticles

Gold Nanorods:Preparation and Influencing Factors on Its Synthesis

Morphological control of seedlessly-synthesized gold nanorods using binary surfactants

Iodide Ions Control Seed-Mediated Growth of Anisotropic Gold Nanoparticles

Gold Nanorods: Synthesis, Growth Mechanism and Purification

Synthesis and Optical Properties of Gold Nanorods with Controllable Morphology.

Seed-Mediated Synthesis of Gold Nanorods at Low Concentrations of CTAB

High Yield Seedless Synthesis of Mini Gold Nanorods: Partial Silver Decoupling Enabling Effective Nanorods Elongation With Tunable Surface Plasmon Resonance Beyond 1000 nm and CTAB-Free Functional Coating for mTHPC Conjugation

A Simple and Effective Route for the Synthesis of Crystalline Silver Nanorods and Nanowires

Shape-Controlled Syntheses of Silver Nanoparticles: Role of the Seeds

High yield seedless synthesis of mini gold nanorods: partial silver decoupling allows effective nanorod elongation with tunable surface plasmon resonance beyond 1000 nm and CTAB-free functional coating for m THPC conjugation

The Morphology Control on the Preparation of Silver Nanotriangles

A Novel Method to Prepare High-Aspect Ratio Gold Nanorods

The Influence of Synthesis Condition and Aging Process of Silver Nanocrystals on the Formation of Silver Nanorods

Seedless Synthesis of High Aspect Ratio Gold Nanorods with High Yield

Controlled Synthesis of Ag Ordered Nanorods

New rule and growth model for the synthesis method of gold nanorods with binary surfactant CTAB and NaOL