Microstructure and Corrosion Properties of AZ91D Magnesium Alloy by Molten Salt Bath Treatment

何美凤,刘磊,仵亚婷,田福英,胡文彬
DOI: https://doi.org/10.3969/j.issn.1001-4381.2010.04.020
2010-01-01
Abstract:A dense and adhesive multilayer coating on AZ91D magnesium was successfully obtained by AlCl3-NaCl molten salt bath treatment.The corrosion resistance of AZ91D alloy without and with coating by a multilayer Mg-Al intermetallic compound was evaluated by open circuit potential and electrochemical impedance spectroscopy measurements in 3.5%(mass fraction)NaCl solutions.A multilayer structure was observed in the alloyed coating at 400℃ with 8h treatment time.The inner layer of alloyed coating presents network feature,while the outer layer of alloyed coating is composed of cubical shape particles.The coated sample shows higher open circuit potential than the uncoated one.The coating polarization resistance value of the coated sample is ten times greater.