Abstract:In this paper, we report the synthesis of hexagonally ordered aluminum-containing mesoporous silica, Al-MCM-41, from natural attapulgite (Al-substituted Si8O2Mg5(OH)(2)(H2O)(4)center dot 4H(2)O) without addition of silica or aluminum reagents. A pretreatment process involving sequential mechanical grinding and acid leaching is critical to the Successful use of attapulgite as a source of both Si and AI in the surfactant-templated hydrothermal synthesis of Al-MCM-41. The resulting mesophase had a surface area of 1030 m(2)/g and an average pore diameter of 3.7 nm with narrow pore size distribution. The influence of changes in processing parameters, such as grinding time, hydrothermal conditions, and calcination temperature, on the textural characteristics of the Al-MCM-41 products is studied. Investigations of the mechanism of structural evolution indicate that grinding of attapulgite results in amorphization and partial structural breakdown, transformation of the fibrous mineral bundles into rod-shaped particles, and partial displacement of octahedrally coordinated Al3+ ions into the Si-O tetrahedral framework. Subsequent acid etching dissolves the Mg-rich octahedral sheets to produce samples with variable texture due to modifications in the residual aluminum-containing silicate sheets and associated silica fragments. Solid-state magic-angle spinining NMR spectroscopy indicates that Al3+ ions are located in both octahedral and tetrahedral sites in the as-synthesized Al-MCM-41 samples, but that the calcined products consist primarily of Al3+ ions substituted in the tetrahedrally coordinated silica matrix of the ordered channel wall structure.

Large Surface Area Mesoporous Al2O3 from Kaolin: Methodology and Characterization

Novel Synthesis and Characterization of Nanosized Γ-Al2o3 from Kaolin

Investigation of the physicochemical aspects from natural kaolin to Al-MCM-41 mesoporous materials.

A Novel Method for Synthesis of Co–Al Layered Double Hydroxides and Their Conversions to Mesoporous CoAl2O4 Nanostructures for Applications in Adsorption Removal of Fluoride Ions

Preparation and Characterization of an Aluminosilicate Material with Layer Expansion Structure

Synthesis and characterization of mesoporous aluminosilicate molecular sieve from K-feldspar

Synthesis of New Kaolin Molecular Sieves from Kaolin and Its Adsorption of Nh4+

Catanionic-surfactant templated synthesis of organized mesoporous γ-alumina by double hydrolysis method

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Research on performance of acid and alkali modified kaolins: II. Surface area and pore structure

Hydrothermal Synthesis of High Surface Area Mesoporous Lithium Aluminate

Catanionic-Surfactant Templated Synthesis Of Organized Mesoporous Gamma-Alumina By Double Hydrolysis Method

From natural attapulgite to mesoporous materials: methodology, characterization and structural evolution.

The Morphologically Controlled Synthesis and Application of Mesoporous Alumina Spheres

Synthesis of Stable Mesoporous Molecular Sieve from Kaolin

Direct Synthesis of Mesoporous Aluminosilicate Using Natural Clay from Low-Grade Potash Ores of A Salt Lake in Qinghai, China, and Its Use in Octadecylamine Adsorption

Modified Inverse Micelle Synthesis for Mesoporous Alumina with a High D4 Siloxane Adsorption Capacity

Preparation of Mesoporous Analcime/Sodalite Composite from Natural Jordanian Kaolin

Cleaner Synthesis of Mesoporous Alumina from Sodium Aluminate Solution

Hydrothermal Synthesis of LiAlO2 Nanostructures with High Specific Surface Area by Using Anodized Aluminum Oxide Template

Gas-Liquid Interfacial Deposition Synthesis of Alumina with Large Mesopores