Research on microstructures and mechanical properties of T92/S304H dissimilar weld joint

Jian Cao,LiNa Ji,Yi Gong,Chao Yang,Cheng Yao,Zhenguo Yang,Xiaoming Luo,FuMing Gu
2010-01-01
Abstract:Microstructures and mechanical properties of the T92/S304H dissimilar weld joints obtained by GTAW were investigated. Results revealed that the T92 base material, which was the weakest region of the joint, and the T92 HAZ respectively exhibited a tempered lath martensitic and a sorbitic microstructure, and carbides like M23C6 and MC were distributed in the grains and on the grain boundaries of them. Weld metal was dendritic austenite and second-phase particles dispersed within its grains. Microstructures of S304H base material and S304H HAZ were austenites, whose grains and grain boundaries were both distributed with precipitates including NbC, NbN and Cu-rich phase as well, resulting in refining and strengthening of the microstructures in return. Comprehensively speaking, the T92/S304H dissimilar weld joints were qualified according to specifications.
What problem does this paper attempt to address?