Abstract:A carbon coated Li3V2(PO4)3 cathode material for lithium ion batteries was synthesized by a sol–gel method using V2O5, H2O2, NH4H2PO4, LiOH and citric acid as starting materials, and its physicochemical properties were investigated using X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) spectroscopy, scanning electron microscopy (SEM), energy dispersive analysis of X-ray (EDAX), transmission electron microscope (TEM), and electrochemical methods. The sample prepared displays a monoclinic structure with a space group of P21/n, and its surface is covered with a rough and porous carbon layer. In the voltage range of 3.0–4.3V, the Li3V2(PO4)3 electrode displays a large reversible capacity, good rate capability and excellent cyclic stability at both 25 and 55°C. The largest reversible capacity of 130mAhg−1 was obtained at 0.1C and 55°C, nearly equivalent to the reversible cycling of two lithium ions per Li3V2(PO4)3 formula unit (133mAhg−1). It was found that the increase in total carbon content can improve the discharge performance of the Li3V2(PO4)3 electrode. In the voltage range of 3.0–4.8V, the extraction and reinsertion of the third lithium ion in the carbon coated Li3V2(PO4)3 host are almost reversible, exhibiting a reversible capacity of 177mAhg−1 and good cyclic performance. The reasons for the excellent electrochemical performance of the carbon coated Li3V2(PO4)3 cathode material were also discussed.

Synthesis and electrochemical performances of Li3V2(PO4)3/(Ag + C) composite cathode

Synthesis and the Improved High-Rate Performance of Limn2o4/Ag Composite Cathode for Lithium-Ion Batteries

Synthesis and Electrochemical Performance of 0.6li3v2(po4)3·0.4li–v–o Composite Cathode Material for Lithium Ion Batteries

Synthesis and characterization of Li3V(2−2x/3)Mgx(PO4)3/C cathode material for lithium-ion batteries

Synthesis of Plate-Like Li3V2(PO4)3/C As a Cathode Material for Li-ion Batteries

Electrochemical Performance of Nanocrystalline Li3V2(PO4)3/carbon Composite Material Synthesized by a Novel Sol–gel Method

Nanostructured Li 3 V 2 (PO 4 ) 3 /C Composite As High-Rate and Long-Life Cathode Material for Lithium Ion Batteries

Carbon-coated Li3V2(PO4)(3) Composite Cathode Material for Lithium-Ion Batteries: Sol-gel Synthesis and Performance

Enhanced electrochemical performance of LiVPO4F/C composite with in-situ generated Li3V2(PO4)3 for lithium-ion batteries

Li3v2(Po4)(3)/C Composite As an Intercalation-Type Anode Material for Lithium-Ion Batteries

Synthesis and electrochemical performance of lithium vanadium phosphate and lithium vanadium oxide composite cathode material for lithium ion batteries

Electrochemical Performance of Li3v2(Po4)(3)/C Cathode Materials Using Stearic Acid As A Carbon Source

Composites of LiMnPO4 with Li3V2(PO4)3 for Cathode in Lithium-Ion Battery

Synthesis and Characterization of Carbon-Coated Li3V2(PO4)3 Cathode Materials with Different Carbon Sources

High Performance Li3V2(PO4)3/C Composite Cathode Material for Lithium Ion Batteries Studied in Pilot Scale Test

Electrochemical performance of the carbon coated Li3V2(PO4)3 cathode material synthesized by a sol–gel method

Synthesis and characterization of LiFePO4/(Ag + C) composite cathodes with nano-carbon webs

Synthesis and electrochemical characterization of LiFePO4/C Cathode materials for Li-ion batteries

Influence of Electrode Design on the Electrochemical Performance of Li3V2(PO4)3/C Nanocomposite Cathode in Lithium Ion Batteries

Novel synthesis of LiFePO4–Li3V2(PO4)3 composite cathode material by aqueous precipitation and lithiation

Electrochemical Performance of LiFe1−xVxPO4/carbon Composites Prepared by Solid-State Reaction