Abstract:To use solar irradiation or interior lighting efficiently, a new photocatalyst with high catalytic activity in visible light was sought. In this work, an upconversion luminescence agent, 40 CdF2·60 BaF2·1.0 Er2O3, was synthesized and its fluorescent spectrum was determined. It is found that this upconversion luminescence agent can emit five upconversion fluorescent peaks below 387nm under the excitation of 488nm visible light. The upconversion luminescence agent has revealed an improvement over ordinary titanium dioxide (TiO2) in photocatalytic activity under visible light irradiation for the photocatalytic degradation of ethyl violet in aqueous solution as a model compound. The TiO2 photocatalyst doped with upconversion luminescence agent was characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM). The photocatalytic degradation of ethyl violet was tracked by UV–vis and 1H-NMR spectra, and the influences of irradiation time, initial concentration of ethyl violet, addition amount of TiO2 catalyst and initial pH value were also investigated. To affirm the complete mineralization, the total organic carbon (TOC) was also tested. The degradation rate of ethyl violet in the presence of doped rutile TiO2 photocatalyst reached 87.08% at 4.0h visible light irradiation, which was obviously higher than the corresponding degradation rate (35.42%) in the presence of undoped rutile TiO2 powder. The research results show that the upconversion luminescence agent is necessary to transform visible lights into ultraviolet lights and thus make the best use of visible lights. By calculation, the upconversion efficiency of the emission peak at 380nm was estimated to be about 0.78%. The TiO2 powder doped upconversion luminescence agent under visible light irradiation is able to decompose the ethyl violet in aqueous solution efficiently, therefore, this method may be envisaged as a technology for treating dyes wastewaters using solar energy, especially at textile industries in developing countries.

Sol-gel preparation of Fe-doped mixed crystal TiO 2 powder and its photocatalytic activity for degradation of azo fuchsine under visible light irradiation

Preparation of Fe-doped Mixed Crystal TiO2 Catalyst and Investigation of Its Sonocatalytic Activity During Degradation of Azo Fuchsine under Ultrasonic Irradiation.

Visible-Light-Driven Titania/Silica Photocatalyst Co-Doped with Boron and Ferrum

Influence of Fe2o3 Doping on Morphology and Photocatalytic Activity of Tio2 Prepared by Adsorption Phase Synthesis

Preparation of Er3+:YAlO3/Fe-doped TiO2–ZnO and its application in photocatalytic degradation of dyes under solar light irradiation

Photocatalytic Degradation of Organic Dyes by a High Efficient TiO<sub>2</sub>-Based Catalysts Under Solar Light Irradiation

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Investigation on degradation of dyestuff wastewater using visible light in the presence of a novel nano TiO2 catalyst doped with upconversion luminescence agent

Investigation on photocatalytic degradation of ethyl violet dyestuff using visible light in the presence of ordinary rutile TiO2 catalyst doped with upconversion luminescence agent.

Sol-Gel Hydrothermal Synthesis and Visible Light Photocatalytic Degradation Performance of Fe/N Codoped TiO2 Catalysts

Synthesis of Fe-doped ZnO by supercritical antisolvent precipitation for the degradation of azo dyes under visible light

Hydrothermal synthesis of hydrangea-like F-doped titania microspheres for the photocatalytic degradation of carbamazepine under UV and visible light irradiation

Nanocrystalline Fe/TiO2 Visible Photocatalyst with a Mesoporous Structure Prepared via a Nonhydrolytic Sol-Gel Route

Preparation of acidic Fe-SiO2 catalyst and its catalytic reactivity in photo-Fenton reaction

F and Fe co-doped TiO<sub>2</sub> with enhanced visible light photocatalytic activity

F and Fe co-doped TiO 2 with enhanced visible light photocatalytic activity

Preparation Of Fe3+-Doped Tio2 Nanoparticles And Their Photocatalytic Activities

Visible-Light Responsive Zinc Ferrite Doped Titania Photocatalyst for Methyl Orange Degradation

Preparation, Characterization and Electronic Structures of Fe-doped TiO2 Nanostructured Fibers

Synthesis of FeTiO3/TiO2 composites by a cross-linking method for enhanced photocatalytic degradation of 4-chlorophenol and dyes

Synergistic effect of Fe doping and oxygen vacancy in AgIO 3 for effectively degrading organic pollutants under natural sunlight