Investigation on magnetic properties and thermal stability for nanocrystalline γ'-Fe4N thin films

Lili Wang,Tao An,LiJun Song,Xin Wang,Jie Gong,Weitao Zheng

2010-01-01

Abstract:Nanocrystalline γ'-Fe4N thin films were synthesized on single crystal Si(100) substrate by facing target magnetron sputtering and were heat-treated in vacuum at different temperatures of 300, 400, 500, 600, 700 and 800°C in order to investigate their thermal stability. The structure, morphology and magnetic properties were characterized using X-ray diffraction(XRD), scanning electron microscopy(SEM) and vibrating sample magnetometer(VSM), respectively. The results indicated that Fe8N capsule layer was formed at the interface of γ'-Fe4N grain between the heat-treating temperature of 300 and 500°C. At heat-treating temperature of 600°C, the Fe8N phase layer tended to decompose to the more stable phase α-Fe. The complete phase transformation from nanocrystalline γ'-Fe4N phase to α-Fe phase occurred at 700°C. The obvious changes of the structure and soft ferromagnetic properties were not found under the temperature of 600°C.