High-Speed Growth of Tio2 Nanotube Arrays with Gradient Pore Diameter and Ultrathin Tube Wall under High-Field Anodization

Xiaoliang Yuan,Maojun Zheng,Li Ma,Wenzhong Shen

DOI: https://doi.org/10.1088/0957-4484/21/40/405302

IF: 3.5

2010-01-01

Nanotechnology

Abstract:Highly ordered TiO2 nanotubular arrays have been prepared by two-step anodization under high field. The high anodizing current densities lead to a high-speed film growth (0.40–1.00 µm min − 1), which is nearly 16 times faster than traditional fabrication of TiO2 at low field. It was found that an annealing process of Ti foil is an effective approach to get a monodisperse and double-pass TiO2 nanotubular layer with a gradient pore diameter and ultrathin tube wall (nearly 10 nm). A higher anodic voltage and longer anodization time are beneficial to the formation of ultrathin tube walls. This approach is simple and cost-effective in fabricating high-quality ordered TiO2 nanotubular arrays for practical applications.