Abstract:Polystyrene nano-microspheres were synthesized by emulsion polymerization methods.The magnetic metal/polymer nanocomposite microspheres were fabricated by electroless nickel plating on the surface of the nano-microspheres.Then morphology,structure and chemical composition of coated and un-coated nano-microspheres were characterized by transmission electron micrography (TEM),X-ray diffraction(XRD) and energy dispersive spectrum analysis (EDS).Magnetic properties of magnetic polystyrene nanocomposite microspheres in various preparation technologcial conditions were tested by vibrating sample megnetometer(VSM).The results show that the activation technology,reductant concentration,bath pH and temperature have remarkable influences on the magnetic properties of coated nano-microspheres.Accroding to the results of the magnetic properties,by optimizing process paramaters,the magnetic Ni/PS core-shell nanocomposite microspheres with the uniform and complete Ni-coating which are about 100nm diameter,regular-shaped and monodisperse were obtained.And this kind of magnetic microspheres can obtain the maximum saturation magnetization Ms=8.8764 emu/g.

Fabrication and Magnetic Properties of Ni/PS Core-Shell Nanocomposite Microspheres