Electrocatalytic characterisics of copper modification of Pd/C cathode catalysts for use in direct methanol fuel cells

Na ZHANG,MengQiu JIA,YaoWu WANG,JianWei GUO,XiaoFeng XIE

DOI: https://doi.org/10.3969/j.issn.1671-4628.2010.01.016

2010-01-01

Abstract:A series of carbon-supported 20% Pd-Cu/C catalysts for use in direct methanol fuel cells (DMFC) have been prepared by an impregnation method. The electrocatalytic characteristics of the catalysts with different contents of Cu were compared. The effects of Cu on the crystal structure and the elemental states in the catalysts were inves-tigated by XRD and ICP. The results show that the catalysts had been completely reduced, and the molar ratio of Pd to Cu in the catalysts accorded well with the quantities added. The Pd-Cu/C catalysts were shown to have the face centered cubic crystal structure. This could indicate that the addition of Cu shortened the Pd-Pd distances in the crystal lattice, and therefore-HO_(2ads) and O-O could be better adsorbed on the surface of the catalyst. When NaBH_4 was used as the reducing agent, and the atomic ratio of Pd to Cu was 3:1, the resulting catalysts had an av-erage particle size of 3.4 nm and showed the best catalytic performance. The electrochemical active surface area of Pd_3Cu/C was 38.9 m~2/gPd and the oxidation reduction reaction (ORR) activity of the Pd_3Cu/C catalyst was much higher than that of the Pd/C catalyst. The electrochemical activity of the Pd_3Cu/C catalyst was comparable to that of a commercial Pt/C catalyst.