Abstract:In this paper, the upconversion luminescent properties of Y2O3:Er3+(1 %)/Yb3+(4%) nanoparticles with different sizes. (13-55 nm) and its corresponding bulk material as a function of excitation power were studied under 978-nm excitation. Red (F-4(9/2) -> I-4(15/2)), green (H-2(11/2), S-4(3/2) -> I-4(15/2)), and blue (H-2(9/2) -> I-4(15/2)) transitions were observed. The results indicated that the relative intensity of the blue as well as the red to the green increased gradually with decreasing particle size. As a function of excitation power, the slope in the In-In plot for the red emission changed between 2.0 and 1.0 and gradually decreased with increasing particle size, which was attributed to competition between linear decay and upconversion processes for the depletion of the intermediate excited states. As the particle size decreased to 13 nm, a three-photon populating process occurred for the green emission. As the excitation power varied in different paths, gradually increasing or gradually decreasing, a hysteresis loop appeared in the power dependence of emission intensity, which was mainly caused by a local thermal effect induced by laser irradiation. The intensity ratio of H-2(11/2) -> I-4(15/2) to S-4(3/2) -> I-4(15/2) (RHs) varied complicatedly with excitation power, which was theoretically explained considering the thermal distribution and relaxation processes. Two novel cross-relaxation paths were proposed on the basis of the variation of R-HS under excitation at different wavelengths, 488 and 978 nm.

Effect of Surface-Absorbing Chemical Groups on the Luminescence of Yb3+/Er3+ Co-Doped Nanosized Y2o3

The Enhancement of 1.5 μm near infrared luminescence in Er3+ and Yb3+ codoped Y2O3 nanocrystalline

[The enhancement of 1.5 microm near infrared luminescence in Er3+ and Yb3+ codoped Y2O3 nanocrystalline].

Size-Dependent Upconversion Luminescence in Er3+/Yb3+-Codoped Nanocrystalline Yttria: Saturation and Thermal Effects

The Preparation and the Up and Down-Conversion Luminescence of Y_2O_2S∶Er,Yb Nanocrystals

Controllable Synthesis and Size-Dependent Upconversion Luminescence Properties of Lu2O3:Yb3+/Er3+ Nanospheres

Preparation and Near-Infrared Luminescence Properties of Y 2 O 3 :Er 3+ , Yb 3+ Nanopowders

Luminescence Spectroscopy and Near-Infrared to Visible Upconversion in Er3+ and Yb3+ Codoped Sc2O3 Nanoparticles

Photoluminescence properties and pump-saturation effect of Er 3+/Yb 3+ co-doped Y 2Ti 2O 7 nanocrystals

Preparation and upconversion luminescence of Er 3 +/Yb 3 + codoped Y 2Ti 2O 7 nanocrystals

Controllable Synthesis and Upconversion Luminescenceof NaYF4:Yb3+, Er3+ Nanocrystals

Structure and Up-Conversion Luminescence Properties of Er(3+)-Yb(3+)Co-Doped Tio(2) Nanocrystals Prepared by Sol-Gel Method

Fabrication and Up-Conversion Luminescence of Er3+:Y2O3 Nanoparticles

Upconversion Luminescence Properties of Y2o3:Yb, Er and Y2o2s:Yb, Er Nanoparticles Prepared by Complex Precipitation

Preparation and Upconversion Emission of Nanocrystalline ZrO2:Er3+-Yb3+

Effect of Li+ Ions Doping on Microstructure and Upconversion Emission of Y2Ti2O7:Er3+/Yb3+ Nanophosphors Synthesized Via a Sol–Gel Method

Controlling Red Upconversion Luminescence in Gd2O3:Yb3+–Er3+ Nanoparticles by Changing the Different Atmosphere

Tunable Upconversion Luminescence of Monodisperse Y2O3: Er3+/Yb3+/Tm3+ Nanoparticles

Size-controlled synthesis and red up-converted luminescence of CeO2:Yb3+/Er3+ nanospheres

Upconversion Luminescence, Intensity Saturation Effect, and Thermal Effect in Gd2o3 : Er-3,Yb3+ Nanowires

The preparation of Y;O;:Er,Yb nanocrystals and study on luminescence properties of visible and infrared emission