PREPARATION AND PROPERTIES OF BIODEGRADABLE COPOLYMER MICELLE@GOLD NANOSHELLS
Hai-Jian Yuan,Chang-Ming Dong
DOI: https://doi.org/10.3724/sp.j.1105.2013.12225
2013-01-01
Acta Polymerica Sinica
Abstract:Poly (epsilon-caprolactone) -b-poly (L-lysine) (PCL-b-PLys) that was synthesized by ring-opening polymerization, self-assembled into spherical micelles with PCL core and PLys shell in aqueous solution, and the intensity-averaged diameter was about 287 nm. Using the micelle as template, HAuCl4 was reduced by HCHO in basic solution (i. e., pH > 10) and with ultrasonication for 4 min, the coordination of the primary amines of PLys with gold resulted in the growth and accumulation of gold in the micellar shell, and finally led to the formation of the micelle@ gold nanoshell. To the best of our knowledge,the micelle@ gold nanoshell was prepared for the first time, and then fully characterized by UV-Vis, XPS, WXRD, TEM, DLS, TGA, photothermal conversion and in vitro tumor cell-killing experiment. The average diameter of the micelle@ gold nanoshell was about 380 nm, which was about 30% similar to 40% bigger than the original micelle, and the mass fraction of gold accounted for about 2/3. Moreover, it showed strong surface plasmon resonance absorption in the near infrared region, and gave a high photothermal conversion efficiency of 63%. After near-infrared laser irradiation for 10 min, about 60% of Hela cells were killed, while the gold nanoshells had low cytotoxicity. Collectively,the micelle@ gold nanoshells demonstrated good biocompatibility, and could efficiently kill tumor cells in vitro,making them potential for photothermal tumor therapy.