Abstract:BACKGROUND: Poly(propylene carbonate) (PPC) is a new synthetic polyester with good mechanical properties and biocompatibility, but it also lacks of bioactivity as other synthetic polymers. Nanofibrous chitosan shows an excellent bioactivity. However, nanofibrous chitosan is hard to fabricate a three dimensional network with a high mechanical property. OBJECTIVE: To fabricate three dimensional poly(propylene carbonate)/chitosan nanofibers (PPC/CSNF) composite porous scaffolds with good mechanical properties and bioactivity by combining PPC and CSNF. METHODS: PPC porous scaffold was firstly fabricated by combining a solution-casting and a porogen-leaching technique, followed by in situ phase separation of chitosan solution within the PPC scaffold to form PPC/CSNF composite porous scaffold. The morphology of PPC and PPC/CSNF scaffolds were observed by a scanning electron microscope (SEM). The compressive modulus and porosity of the scaffolds were characterized. The cell growth after PPC/CSNF scaffold being subepidermally implanted in the leg of New Zealand rabbit for one and two months was also evaluated by SEM observation. RESULTS AND CONCLUSION: A PPC porous scaffold with interconnected pores of 200-500 μm was fabricated. The diameter of chitosan nanofibers in the PPC/CSNF scaffold varied from 50 nm to 500 nm. All the scaffolds showed a high porosity of over 90%. The compressive modulus of various scaffolds increased with the concentration of PPC and reached a maximum of about 15 MPa, which met the mechanical requirement of cartilage tissue engineering scaffolds. The implant results showed that PPC/CSNF porous scaffold had good bioactivity and was able to induce the differentiation of bone marrow stromal cells of New Zealand rabbit into chondrocytes. A three dimensional PPC/CSNF composite porous scaffold with good mechanical properties and bioactivity was successfully fabricated by combing a phase separation and a solution-casting/porogen-leaching technique. The PPC/CSNF composite scaffold could promote the differentiation of bone marrow stromal cells of New Zealand rabbit into chondrocytes.

Construction and property of three-dimensional poly(propylene carbonate), chitosan nanofibers composite porous scafrolds

From Common Biomass Materials to High-Performance Tissue Engineering Scaffold: Biomimetic Preparation, Properties Characterization, in Vitro and in Vivo Evaluations

Engineering cartilage tissue based on cartilage-derived extracellular matrix cECM/PCL hybrid nanofibrous scaffold

Fabrication and in vivo osteogenesis of biomimetic poly(propylene carbonate) scaffold with nanofibrous chitosan network in macropores for bone tissue engineering

Preparation of Open-Porous Stereocomplex PLA/PBAT Scaffolds and Correlation Between Their Morphology, Mechanical Behavior, and Cell Compatibility.

Fabrication and in vivo chondrification of a poly(propylene carbonate)/L-lactide-grafted tetracalcium phosphate electrospun scaffold for cartilage tissue engineering

Preparation and Properties of Biomimetic Porous Nanofibrous Poly(l-Lactide) Scaffold with Chitosan Nanofiber Network by a Dual Thermally Induced Phase Separation Technique.

Microporous polylactic acid/chitin nanocrystals composite scaffolds using in-situ foaming 3D printing for bone tissue engineering

Bio-Inspired Fabrication of Polymer Composite Scaffolds with Chitosan Network Inside the Pore Channels

Development and Characterization of Functional Polylactic Acid/Chitosan Porous Scaffolds for Bone Tissue Engineering

Preparation and Biological Properties of a Novel Composite Scaffold of Nano-Hydroxyapatite/chitosan/carboxymethyl Cellulose for Bone Tissue Engineering

Characterization and Osteogenic Evaluation of Mesoporous Magnesium–calcium Silicate/polycaprolactone/polybutylene Succinate Composite Scaffolds Fabricated by Rapid Prototyping

Preparation and properties of nano-hydroxyapatite/chitosan/carboxymethyl cellulose composite scaffold

Macroporous Poly (L-Lactic Acid)/chitosan Nanofibrous Scaffolds Through Cloud Point Thermally Induced Phase Separation for Enhanced Bone Regeneration

Enhanced Cell Ingrowth and Proliferation Through Three-Dimensional Nanocomposite Scaffolds with Controlled Pore Structures

Fabrication of polycaprolactone scaffolds filled with cell‐compatible porous matrix for enhanced cell growth for biomedical applications

Performance of 3D printed porous polyetheretherketone composite scaffolds combined with nano-hydroxyapatite/carbon fiber in bone tissue engineering: a biological evaluation

Fabrication and Properties of Poly(L-Lactide)/Hydroxyapatite/Chitosan Fiber Ternary Composite Scaffolds for Bone Tissue Engineering

Preparation Of Chitosan/Silkfibroin/Hydroxyapatite Porous Scaffold And Its Characteristics In Comparison To Bi-Component Scaffolds

Fabrication and biocompatibility of nano non-stoichiometric apatite and poly(epsilon-caprolactone) composite scaffold by using prototyping controlled process

Mechanical Enhancement and in Vitro Biocompatibility of Nanofibrous Collagen-Chitosan Scaffolds for Tissue Engineering