Photocatalytic Water Splitting by Band-Gap Engineering of Solid Solution Bi1−xDyxVO4 and Bi0.5M0.5VO4 (M = La, Sm, Nd, Gd, Eu, Y)
Qizhao Wang,Ning An,Ruijuan Mu,Hui Liu,Jian Yuan,Jianwei Shi,Wenfeng Shangguan
DOI: https://doi.org/10.1016/j.jallcom.2012.01.017
IF: 6.2
2012-01-01
Journal of Alloys and Compounds
Abstract:A series of metal oxide solid solutions Bi1-xDyxVO4 and Bi0.5M0.5VO4 (M = La, Sm, Nd, Gd, Eu, Y) were synthesized by solid state reaction at high temperature and characterized by XRD, UV-vis DRS, BET, SEM. Bi1-xDyxVO4 showed two crystal structures with the component content. For 0.3 <= x <= 1.0, the structure was tetragonal type, while that was monoclinic when x = 0. For 0.1 <= x < 0.3, tetragonal and monoclinic structures had been observed. Bi1-xDyxVO4 solid solutions of tetragonal type could split water into H-2 and O-2 simultaneously when loaded with 0.3 wt% Pt and 1 wt% Pt-Cr2O3 respectively as cocatalyst. Among these catalysts, Bi0.5Dy0.5VO4 showed the best photocatalytic activity for water splitting under UV light irradiation. Besides, Bi0.5M0.5VO4 (M = La, Sm, Nd, Gd, Eu, Y) were also prepared and discovered to be of tetragonal type as same as Bi0.5Dy0.5VO4. They performed high photocatalytic activities of splitting pure water into H-2 and O-2 under UV light irradiation when loaded with 1 wt% Pt-Cr2O3. The activities of Bi0.5M0.5VO4 (M = Dy, La, Sm, Nd, Gd, Eu, Y) solid solutions indicated band-gap engineering of metal oxide solid solutions was the feasible method to obtain a photocatalyst for overall water splitting. Crown Copyright (C) 2012 Published by Elsevier B. V. All rights reserved.