Enhanced Dielectric and Energy-Storage Properties in BiFeO3-modified Bi-0.5(Na0.8K0.2)(0.5)TiO3 Thin Films
Pan Chen,Peng Li,Jiwei Zhai,Bo Shen,Feng Li,Shuanghao Wu
DOI: https://doi.org/10.1016/j.ceramint.2017.07.039
IF: 5.532
2017-01-01
Ceramics International
Abstract:Lead free Bi0.5(Na0.8K0.2)0.5TiO3 thin films doped with BiFeO3 (abbreviated as BNKT-xBFO) (x = 0, 0.02, 0.04, 0.08, 0.10) were deposited on Pt(111)/Ti/SiO2/Si substrates by sol-gel/spin coating technique and the effects of BiFeO3 content on the crystal structure and electrical properties were investigated in detail. The results showed that all the BNKT-xBFO thin films exhibited a single perovskite phase structure and high-dense surface. Reduced leakage current density, enhanced dielectric and ferroelectric properties were achieved at the optimal composition of BNKT-0.10BFO thin films, with a leakage current density, dielectric constant, dielectric loss and maximum polarization of < 2 × 10−4A/cm3, ~ 978, ~ 0.028 and ~ 74.13μC/cm2 at room temperature, respectively. Moreover, the BNKT-0.10BFO thin films possessed superior energy storage properties due to their slim P-E loops and large maximum polarization, with an energy storage density of 22.12J/cm3 and an energy conversion efficiency of 60.85% under a relatively low electric field of 1200kV/cm. Furthermore, the first half period of the BNKT-0.10BFO thin film capacitor was about 0.15μs, during which most charges and energy were released. The large recoverable energy density and the fast discharge process indicated the potential application of the BNKT-0.10BFO thin films in electrostatic capacitors and embedded devices.