The microstructure and properties of in-situ TiB2/6351 Al composites after hot extrusion

Sheng-li GUO,De-fu LI,Dong CHEN,Hao-wei WANG
DOI: https://doi.org/10.3969/j.issn.1007-2012.2009.03.035
2009-01-01
Abstract:The microstructure and properties of the in-situ TiB2(wt,8%)/6351 Al composites before and after extrusion were studied by means of optical morphology,scanning electronic microscopy,transmission electronic microscopy and universal testing machine.The results show that hot extrusion deformation made the particles distribution more homogeneous in matrix alloy and the interface between TiB2 particles and matrix alloy is good bonding without interface cracking.During the hot extrusion deformation,the more complex dislocation structures were formed around the TiB2 particles.Recrystallization and recovery occurred,fine equiaxed grains and substructures existed in matrix and the microstructure was refined.It is noted that the accumulation of dislocations in the vicinity of TiB2 particles leading to these regions becoming sites for recrystallization nucleation,the subgain coalescent and strain-induced boundary migration(SIBM)were main recrystallization nucleation mechanism.The[111] texture was formed in matrix during the hot extrusion deformation.Compared whit cast ingot,the yield strength,tensile strength,elongation rate and hardness remarkably enhance.The fracture of the cast composites displayed ductile failure and intergranular fracture.And it displayed ductile failure after extrusion.
What problem does this paper attempt to address?