Study on Bisphenol-A Bis(diphenyl phosphate) Flame-retarded PC/ABS
Lu Lingang,Xu Xiaonan,Yin Quanming,Wang Dawei
DOI: https://doi.org/10.3969/j.issn.1005-3360.2009.03.013
2009-01-01
Abstract:The flame-retardant PC/ABS was prepared by adding self-made bisphenol a bis(diphenyl phosphate)(BDP)and its BDP/APP and BDP/SiO2 compounded systems.The mechanical performances, the limiting oxygen index(LOI), the vertical combustion performances(UL94), the flame retardant performances, the smoke release of bisphenol A diphosphate(BDP), were studied.The results showed that as the content of BDP added in PC/ABS was 15%, the impact strength was reduced by 12.82%, and the PC/ABS resins passed the UL94V—0 test, LOI reached 30.0%.CONE data showed that the average heat rate(av-HRR) and peak heat rate(pk-HRR) reduced by 35.84% and 31.17%, the ignition time(TTI ) increased by 18s, the flame growth index(FGI) reduced by 46.72%, and the specific extinction area(SEA) increased by 6.68%.When the content of 15%BDP/APP, the PC/ABS resins only passed the UL94V—1 test, LOI reached 31.4%, its maximum reduction range of impact strength was 33.33%, the av-HRR and pk-HRR reduced by 40.89 % and 31.2%, the TTI increased by 20s, the FGI reduced by 50.37%, and the SEA increased by 11.14%.Adding BDP and nanometer SiO2 into PC/ABS resin, when the content of nanometer SiO2 was 7%, the impact strength increased by 5.13% , the PC/ABS resins also passed the UL94V—0 test, LOI reached 31.1%, the av-HRR and pk-HRR reduced by 43.18% and 40.69%, the TTI increased by 20s, the FGI reduced by 59.12%, and the SEA increased by 8.09%, but the av-SEA reduced by 6.92% in 6 minute and the total smoke product index in 6 minutes(TSPI6min ) reduced by 5.54%.PC/ABS resin added BDP and nanometer SiO2(7%) had the best flame retardance and suppression smoke effect, and the slightest influence on the physical performances.