Abstract:Amorphous poly(ethylene terephthalate) (PET), which possess a low softening temperature (Ts=75°C), was exploited to fabricate the electrophoresis chip with an integrated gold electrode for amperometric detection, with emphases being focused on the PET surface modification via UV light and air plasma. Both UV irradiation and plasma treatment were found to be able to improve the surface wettability, enhance the supported electroosmotic flow (EOF), and increase thermal bonding strength of PET sheets, with the latter being more efficient and less time-consuming than the former in the surface modification. Upon treated with plasma for 2min, the PET sheets could be thermally bonded at 65°C. T-peer test showed that the bonding strength increased from 10g/cm for native PET sheets to 1250g/cm for the plasma treated sheets when chips were bonded at the softening point, Attenuated-total-internal-reflection spectrum showed that, after being exposed to the UV light, carboxylic groups site-selectively formed in the UV-exposed region on PET surface. These UV-induced carboxylic groups were further utilized as the scaffold for preparation of micro-gold electrode via electroless gold plating. By using this established UV-directed electroless plating and the plasma-assisted thermal bonding techniques, the full PET electrophoresis chip with an integrated micro-gold electrode could be fabricated in common chemistry laboratory without the need of clean rooms. The fabricated PET chips were demonstrated for separation and detection of model analytes of dopamine (DA) and catechol (CA). Satisfactory resolution of the two analytes was achieved within 40s, and detection limits of 0.87μM and 1.28μM for DA and CA were obtained, respectively.

Influence of Pore Size and Pore Shape on Thermo‐sensitive Properties of Poly[(ethylene Terephthalate)‐graft‐(n‐isopropylacrylamide)] Track Membranes

Effects of Physical Aging on Thermomechanical Behaviors of Poly(ethylene Terephthalate)-Glycol (PETG)

Thermally On−Off Switching Membranes Prepared by Pore-Filling Poly(N-isopropylacrylamide) Hydrogels

Preparation of Temperature-Sensitive Track Membrane by Bulk Photografting

Thermo-sensitive switching membranes regulated by pore-covering polymer brushes

Study on the preparation of porous polyethylene glycol terephthalate film and the influencing factors of etching rate

Ultrafast Selective Ionic Transport Through Heat-Treated Polyethylene Terephthalate Track Membranes with Sub-Nanometer Pores

Preparation of Functional Track Membranes by Photografting Polymerization

Characterization of the Surface Charge Property and Porosity of Track-etched Polymer Membranes

Temperature sensitivity and electrokinetic behavior of a N-isopropylacrylamide grafted microporous polyethylene membrane

Influence of Different Molecular Weights and Concentrations of Poly(glycidyl methacrylate) on Recycled Poly(ethylene terephthalate): A Thermal, Mechanical, and Rheological Study

Temperature-sensitive membranes prepared by the plasma-induced graft polymerization ofN-Isopropylacrylamide into porous polyethylene membranes

Configuration and Electrokinetic Phenomena of N-isopropylacrylamide Grafted Polyethylene Microporous Membranes

Graft Polymerization of Stearyl Methacrylate on PET Track-Etched Membranes for Oil–Water Separation

Modification of Amorphous Poly(ethylene Terephthalate) Surface by UV Light and Plasma for Fabrication of an Electrophoresis Chip with an Integrated Gold Microelectrode

Effect of external electric fields on the ionic conductivity of the PET ion-track membrane

Influence of High Frequency Ex-electric Field on Etching Process and Shape of Pores for Nuclear Track Film

Graft polymerization of N-isopropylacrylamide into a microporous polyethylene membrane by the plasma method: technique and morphology

Influence of UV-Irradiation on Latent Tracks in Polyethylene Terephthalate Films

Temperature-responsive poly(tetrafluoroethylene) membranes grafted with branched poly(N-isopropylacrylamide) chains

Effect of PEG Additives on Properties and Morphologies of Polyetherimide Membranes Prepared by Phase Inversion