Crystallographic and thermal expansion properties of rare earth solid solution Er2-xRxMo4O15
Jie Peng,Xiaoling Xiao,Zhongbo Hu,Juzhou Tao
DOI: https://doi.org/10.1016/j.solidstatesciences.2008.03.025
IF: 3.752
2008-01-01
Solid State Sciences
Abstract:Er2−xRxMo4O15 (R=Sm, Nd, Y, Dy) solid solutions were successfully synthesized and their structure characterized by X-ray powder diffraction. All samples are found to crystallize in the monoclinic space group P21/c. Experimental results indicate that amount of Er substitution is restricted in the case of Sm and Nd, with maximal x=0.6. Thermal expansion properties of Er2−xRxMo4O15 (R=Sm, Nd; x=0.0, 0.2, 0.6) and Er1.8R0.2Mo4O15 (R=Y, Dy) were studied by high-temperature X-ray diffraction. For the same substitution content, x=0.2 and through the identical temperature range of 25–500°C, Y shows the strongest effect on the thermal expansion coefficients (TEC), i.e., TECs of Er1.8R0.2Mo4O15 are 2.65×10−5/K, 2.29×10−5/K, 2.58×10−5/K and 2.43×10−5/K for R=Y, Dy, Sm and Nd, respectively, comparing to the TEC of Er2.0Mo4O15 being 1.90×10−5/K. Substitution element type and content can affect the TEC of Er2−xRxMo4O15. Bond length analysis suggests that the Er(R)–O is responsible for the overall positive thermal expansion behaviors of these molybdates.