Flow Stress Behaviors of In-Situ TiB2/6351 Composite During Hot Compression Deformation at Elevated Temperatures

郭胜利,李德富,陈东,王浩伟
DOI: https://doi.org/10.3321/j.issn:1004-0609.2009.01.002
2009-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The flow stress features of in-situ TiB2/6351 composites were studied by isothermal compression at 300-550 ℃ and strain rate of 10-3-10 /s on Gleeble-1500D system. The results show that TiB2/6351 composites have the steady-state flow characteristics and belong to positive strain rate sensitized materials during hot compression deformation. At lower strain rates and higher temperatures,with the increase of strain, the flow stress increases to peak value and then falls down, at last tends to smooth gradually. The curves express the feature of dynamic recrystallization. But at higher strain rates and lower temperatures, dynamic recovery occurs obviously. The flow stress of in-situ TiB2/6351 composites during high temperature compression deformation can be represented by Zener-Hollomon parameter including Arrhenius term. A, α and n in the analytical expressions of flow stress are 3.52×1010 /s, 0.023 MPa-1 and 7.33, respectively, by linear regression analysis and optimization calculation. The hot deformation activation energy of TiB2/6351 composites during hot deformation is 170.10 kJ/mol.
What problem does this paper attempt to address?