Influences of Fluorine Auxochrome in Fluorene Molecular Electroluminescent Material on Optoelectronic Property
ShuangLing Lou,JunSheng Yu,YaDong Jiang,GuoJun Guo,Qing Zhang
DOI: https://doi.org/10.1007/s11434-008-0395-1
2008-01-01
Abstract:The UV-Vis absorption and photoluminescence (PL) spectra of 2,3-bis(9,9-dihexyl-9H-fluoren-2-yl) quinoxaline (Py), 2,3-bis(9,9-dihexyl-9H-fluoren-2-yl)-6,7-difluoroquinoxaline (F2Py) and 2,3-bis(9,9-dihexyl-9H-fluoren-2-yl)-5,6,7,8-tetrafluoroquinoxaline (F4Py), which are fluorene molecular derivatives with conjugated structure, were investigated. For further investigation of the influences of fluorine auxochrome in fluorene molecular electroluminescent material on optoelectronic property, the electroluminescence (EL) characteristics of materials were studied by double-layer organic light-emitting diodes (OLEDs) using N,N′-Di-[(1-naphthalenyl)-N,N′-diphenyl]-(1,1′-biphenyl)-4,4′-diamine (NPB) as a hole transporting layer (HTL) with the conventional vacuum deposition method. The results showed that the absorption and PL spectra of materials in film state red shifted with fluorine substituents increased in molecule configuration. The performance of OLEDs is as follows: at a bias voltage of 5 V, Py emitted a blue-green light at 508 nm with the Commission Internationale d’Eclairage (CIE) coordinates of (0.23, 0.43) and full width at half maximum (FWHM) of 100 nm. The device had a turn-on voltage (defined as the drive voltage at the luminance of 1 cd/m2) of 4.8 V, a luminance of 129 cd/m2 with a current density of 59 mA/cm2 at 10 V, and a maximum luminous efficiency of 0.18 lm/W at 5.4 V. F2Py and F4Py emitted a green light peaking at 544 nm and a yellow light at 570 nm at 5 V, with the CIE coordinates of (0.38, 0.56) and (0.44, 0.49), and FWHM of 103 and 117 nm, respectively. The F2Py and F4Py devices had a turn-on voltage of 4 and 2 V, a luminance of 557 and 3300 cd/m2 with a current density of 100 and 880 mA/cm2 at 10 V, and a maximum luminous efficiency of 0.22 lm/W at 7.6 V and 0.53 lm/W at 2 V, respectively.