Effects of solid solution heat treatment on the microstructures and mechanical properties of Mg96.82Gd2Zn1Zr 0.18 alloy with the 14H-type LPSO structure

Yujuan Wu,Xiaoqin Zeng,Dongliang Lin,L. M. Peng,Guangyin Yuan,Wenjiang Ding
2009-01-01
Abstract:In an as-cast Mg96.82Gd2Zn1Zr0.18 alloy, by optical microscope (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations, the as-cast microstructure was confirmed to be composed of the alpha'-Mg solid solution, and the eutectic in which the second phase is beta-phase ((Mg,Zn)(3)Gd) with a fcc structure and the coherent fine-lamellae. The lamellae consist of the 2H-Mg and the 14H-type long period stacking ordered (LPSO) structure formed in a'-Mg matrix, which has first been observed in the as-cast Mg96.82Gd2Zn1Zr0.18 alloy. Moreover, during subsequent solid solution treatment at 773 K, the microstructure evolutions, especially that of the lamellar 14H-type LPSO structure and the beta-phase were studied. The results indicate that a solid state phase transformation occurs in grain boundaries, i.e., a lamellar X-phase with the 14H-type LPSO structure is transformed from the P-phase. Furthermore, by tensile tests at room temperature, it can be concluded that the alloy solid-solution-treated at 773 K for 10 h exhibits higher tensile strength (246.21 MPa) and larger elongation (11.79%) due to the lamellar X-phase and the fine-lamellae in matrix with 14H-type LPSO structure.
What problem does this paper attempt to address?