PRoPERTIES oF AN ENVIRONMENTALLY FRIENDLY WATERBoRNE ANTISTATIC ANTICORRoSIVE PAINT

Zhonghua CHEN,Ying TANG,Fei YU

DOI: https://doi.org/10.3969/j.issn.1005-4537.2009.02.007

2009-01-01

Abstract:Using light color conductive mica, titanium oxides and environmentally friendly anticorrosive pigments in the two-component epoxy paint system, a new kind of environmentally friendly waterborne paint with good antistatic property, excellent anticorrosion performance and good ornamental behavior was prepared. The antistatic property and anticorrosive performance of the paint were analyzed by use of scanning electron microscopy, laser particle diameter analyzer and surface resistivity tester. The results indicated that the particle size and the amount of conductive mica, its dispersing speed, the amount of titanium oxides, and the type of anti-settlement agent have great influence on the antistatic property of the paint. Combined with 30 mass% conductive mica (of volume average diameter as 16.96μm) under its dispersing speed of 1000 r/min and fumed SiO2 as anti-settlement agent, the surface resistivity of the paint can reach to 106Ω. The optimal addition of titanium oxides is 2.7 mass%. The integrated properties of paint were decided by the ratio of epoxy resin to its curing agent, the pigment volume concentration (PVC) and the type of anticorrosive pigments. As the PVC range from 30% to 35% and the ratio of epoxy resin to its curing agent reach to 4:1, the optimal integrated property of the paint can be obtained.