Biocompatibility between copolymers of 3-hydroxybutyrate and 3-hydroxyvalerate and chondrocytes

Qi-chun Zhao,Dao-zhang Cai

2009-01-01

Abstract:Background: Copolymers of 3-hydro-xybutyrate and 3-hydroxyvalerate (PHBV) is a synthesized product of microorganism in unbalance growth environment, characterizing by degradation and thermoplasticity. It, as a new scaffold material in tissue engineering field, attracts more and more attention. Objective: To evaluate the biocompatibility between PHBV and sheep articular chondrocytes. Design, time and setting: In vitro contrast observational study was performed at Central Laboratory of the Third Hospital Affiliated to Sun Yat-sen University and Animal Surgical Department of Guangdong Guanghao Biotechnology Company between November 2005 and May 2007. Materials: PHBV and foam-like three-dimensional scaffold were provided by Materials College of South China University of Technology. A male sheep aged 6 months and weighing 17 kg was provided by Guangdong Guanghao Biotechnology Company. Methods: Sheep articular chondrocytes were isolated and cultured. The second-passage chondrocytes were seeded onto the PHBV films and foam-like three-dimensional scaffold. Single cell culture was considered as the control. Main outcome measures: The cell form was observed using scanning electron microscopy, and adhesion rate was measured at 1, 2, and 6 hours after seeding. Extract solution was prepared according to amount of culture solution and scaffold volume (10 mL/cm3), while extract solution as 1/16-16 times as normal solution was also prepared. The cell toxicity was measured with MTT assay. The cycle of seeded cells was detected with flow cytometry so as to calculate proliferation index. The DNA content of cells inoculated on PHBV after 4, 8, and 12 days was quantified using the Hoechst 33342 assay, and the glycosaminoglycan (GAG) content was determined by 1, 9-dimethylmethylene blue (DMB) binding assay. Results: Adhesion rate of the second-passage chondrocytes inoculated on PHBV after 6 hours was 75.6%, which was no significant difference compared to control group. MTT assay indicated extract solution of nine gradient concentrations was not toxic. Scanning electron microscopy demonstrated that chondrocytes attached onto PHBV films, extending well and acquiring a flat morphology. Moreover, on the foam-like three-dimensional scaffold, the seeded cells laid in micro-pores and secreted a lot of matrixes. Flow cytometry showed that there was no significant difference in cell cycle between the scaffold and the control groups. GAG concentration in the PHBV group was significantly higher than chondrocytes in the control group at day 8 after inoculation; while, DNA content was also increased on the scaffolds at day 12 after inoculation. Conclusion: PHBV, as a scaffold material of cartilage tissue engineering, has an excellent biocompatibility to sheep articular chondrocytes. But, the adhesion rate is low in the early stage.