Cytotoxity of nickel-titanium shape memory alloys following surface oxidation

Xue Zhang,Yang Zhang,Cui-juan Feng,Qiang Wang

DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.34.009

2009-01-01

Abstract:BACKGROUND: Surface modification on nickel-titanium shape memory alloy (NiTi-SMA) may reduce separation of nickel ions so as to enhance the biocompatibility. OBJECTIVE: To evaluate the cytotoxicity of NiTi-SMA with surface oxidation. DESIGN, TIME AND SETTING: An in vitro study based on materials and cytology level was performed at Central Laboratory, School of Stomatology, China Medical University from November to December 2008. MATERIALS: L-929 cells were provided by Central Laboratory of China Medical University, and NiTi-SMA was provided by Grikin Advanced Materials Co., Ltd., Beijing. METHODS: NiTi-SMA was made into round samples with radius 10 mm and thickness 3 mm which were divided into oxidation group and non-oxidation group. Samples in the oxidation group were ultrasonically rinsed with acetone, dried in the air, oxidated in boiling H2O2 for 2 hours, and ultrasonically cleaned with deionized water; while, the samples in the non-oxidation group were not treated with any materials. Alloy leaching liquor was prepared with RPMI-1640 culture media according to the ratio between surface area and volume of culture solution (3 cm2/mL). The leaching liquor was maintained in incubator at 37°C for 96 hours, and then degerming was performed using microporous membrane. 6.4% phenol was added, which was considered as the positive control group, and 1640 culture media was considered as the blank control group. MAIN OUTCOME MEASURES: Growth of L-929 cells was observed under inverted phase contrast microscope; absorbance of cells cultured for 24 and 48 hours was detected using MTT test; cytotoxicity of NiTi-SMA with surface oxidation was evaluated. RESULTS: Circled digit oneAt 24 hours after culture, cells in the positive control group was abnormal; while, cells in the oxidation, non-oxidation, and blank control groups well adherent-grew. At 48 hours after culture, cytotoxicity was detected out in the positive control group; cells in the oxidation, non-oxidation, and blank control groups were normal and grew well. A few of cells in the non-oxidation group showed karyopyknosis. Circled digit twoAs compared to blank control group, absorbance in the oxidation and non-oxidation groups was increased with the prolongation of culture time (P < 0.05), and the increasing in the oxidation group was significantly higher than non-oxidation group (P < 0.05). Cytotoxicity was grade 0 in the oxidation group at 24 and 48 hours after culture, showing a mild toxicity. In addition, cytotoxicity was grade 0 at 24 hours after culture and grade 1 at 48 hours after culture in the non-oxidation group, showing a remarkable toxicity. Cytotoxicity was not found out in the blank control group. CONCLUSION: The cytotoxicity of NiTi-SMA with surface oxidation is lower than the non-oxide alloy, which is coincidence with the requirement of the clinical application.